1) erosive melting
蚀熔
2) Melting erosion
熔蚀
1.
The results show that with the increased brazing temperature from 595℃ to 615℃,the melting erosion rate increases from 10% to 25%,the false brazing rate decreases from 10% to 2%.
结果表明,钎焊温度从595℃提高到615℃时,熔蚀率从10%提高到25%,虚焊率从10%降低到2%;钎料包覆率从8%提高到16%时,熔蚀率从25%提高到50%。
3) corrosion
[英][kə'rəuʒən] [美][kə'roʒən]
熔蚀
1.
The molten steel corrosion and ultrasonic vibration resistance of a corundum stick,a tungsten alloy stick,a metal Mo stick coated with ZrO2 outside,and a Mo-Al2O3-ZrO2 ceramic metal tube were investigated for ultrasonic treatment of molten steel.
研究了刚玉棒、钨合金棒、外涂ZrO2金属钼棒和Mo-Al2O3-ZrO2金属陶瓷管在钢液中的熔蚀和抗超声波振动的情况。
4) ablation
[英][æb'leiʃən] [美][æb'leʃən]
熔蚀
1.
A unique laser ablation method is proposed to prepare nano crystals in which graphite target is ablated by high power pulsed laser in liquid ,and nano crystalline carbon nitrides are prepared in ammonia solution for the first time.
本文提出一种独特的激光熔蚀法即在液体中激光熔蚀固体靶制备纳米晶，并且首次在氨水中激光熔蚀石墨靶制备出氮化碳纳米晶。
5) the melting corrosion structure
熔蚀结构
1.
The analysis of optical microscope indicates that through the reasonable iron material proportioning,alkalinity,fuel consumption and moisture to promote the calcium ferrite and iron olivine formation,and to obtain the melting corrosion structure or the granular structure as primarily sinter,the sinter strength could be effectively increased.
通过光学显微镜分析表明,合理控制铁料搭配、燃耗、碱度和物料水分等条件,可以生成较多的铁酸钙和铁橄榄石,得到以熔蚀结构或粒(板条)状结构为主的烧结矿,可以有效的提高烧结矿强度。
6) corrosion in melting zinc
熔锌腐蚀
1.
Since ferroalloy is liable to corrosion in melting zinc,it is imperative to evaluate the anticorrosion behavior of the ferroalloy fast and accurately in terms of the selection of the ferroalloy materials.
熔融的液锌对Fe基合金有很强的腐蚀作用,判断Fe基合金的耐熔锌腐蚀性能对选择Fe基合金材料有重要的作用。
补充资料：熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
production of niobium powder by molten salt electrolysis
rongyand+onjlefa ShengChan n.fen熔盐电解法生产妮粉(produetion。fn;obi-um powder by molten salt eleetrolysls)见熔盐电解法生产担粉。