1) high carbon steel wire rod
高碳钢线材
1.
To research the effect of different cooling speed on the microstructure and property of 9 mm high carbon steel wire rod by means of cooling control process and the experiments of microstructure and property and the simulated analysis.
通过控冷工艺、组织性能实验和模拟分析 ,研究了不同冷却速度对 9mm高碳钢线材组织性能的影响。
2.
To research a method for determining Ca content in high carbon steel wire rod with ICP-AES.
研究用ICP-AES光谱仪测定高碳钢线材中钙含量的方法,通过试验建立了最佳工作条件,测定了元素的检出限及测定下限,并进行了干扰试验、准确度试验、回收率试验,试验结果证明:ICP-AES光谱仪测定高碳钢线材中钙含量的方法简便、快速、准确,分析结果满意。
2) high-carbon steel wire
高碳钢线材
1.
Experimental study to reduce brittle inclusion in high-carbon steel wire;
降低高碳钢线材中脆性夹杂物的试验研究
2.
Through simulating with thermal simulator Gleeble-1500 the controlledcooling process of φ9mm high-carbon steel wire after spited out, the effect of the various controlled-cooling process parameters on the mechanical performance of the wire is researched, the best cooling system under the test conditions got, the valuable theoretic reference for practical production offered.
通过利用热模拟机Gleeble-1500对φ9mm高碳钢线材吐丝后控制冷却过程的模拟，研究了控冷工艺参数的变化对高碳钢线材力学性能的影响，得到了试验条件下最佳的控冷工艺制度，为实际生产提供了有价值的理论参考。
3) high carbon steel for tire wire cord
高碳帘线钢线材
4) medium and high carbon steel wire rod
中高碳钢线材
1.
Non-metallic inclusion control technology in medium and high carbon steel wire rod
中高碳钢线材中非金属夹杂物控制技术
5) High Carbon Steel for Tyre Cord Wire
高碳帘线钢
6) high-Carbon steel wirebar
高碳钢线坯
补充资料：高碳钢
分子式：
CAS号：
性质：含碳量大于0.6％的碳素钢，常用含碳量为0.60％～1.50％。除碳外还可含有少量锰(0.70％～1.20％)，如65Mn。高碳钢都属于优质碳素钢或高级优质碳素钢，如T8A等。用高碳钢制成的各种零件，一般都必须经过不同形式的热处理后再使用。因为含碳量较高，热处理后可以较容易得到高强度(σb>980MPa)、高硬度(HRC60以上)以及优良的耐磨性，并具有一定的塑性和韧性。可作为工具钢及弹簧钢等使用。
CAS号：
性质：含碳量大于0.6％的碳素钢，常用含碳量为0.60％～1.50％。除碳外还可含有少量锰(0.70％～1.20％)，如65Mn。高碳钢都属于优质碳素钢或高级优质碳素钢，如T8A等。用高碳钢制成的各种零件，一般都必须经过不同形式的热处理后再使用。因为含碳量较高，热处理后可以较容易得到高强度(σb>980MPa)、高硬度(HRC60以上)以及优良的耐磨性，并具有一定的塑性和韧性。可作为工具钢及弹簧钢等使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。