1) high carbon steel wire
高碳钢丝
1.
To research delamination phenomenon of high carbon steel wire on the view of cementite decomposing during wire drawing and through experiment data.
根据拉丝过程中渗碳体分解的观点,并通过实验数据,对高碳钢丝发生分层现象进行研究。
2.
To introduce the application of pickling free drawing process to semi finished high carbon steel wire production.
介绍无酸洗拉拔工艺在高碳钢丝半成品生产上的应用。
3.
When S-Zn-75 and conductive salt added as additive to an electrogalvanizing productive process of high carbon steel wire,there is a promoting efficiency.
在高碳钢丝的电镀生产过程中 ,采用硫锌 -75及导电盐作为镀液添加剂 ,提高了电镀效率 ,降低了镀锌钢丝在拉拔过程中的镀层损失以及拉丝模的消耗 ,生产成本下降 ,最终成品钢丝绳色泽银白光亮。
2) wire of hi-carbon and low alloy
高碳低合金钢丝
1.
In order to solve the problem of crack deformation tendency of the quenched steel wires for a uniform structure,development is done to the special wire of hi-carbon and low alloy,finding that there is variation of spheroidizing annealing processed structure under the same spheroidizing annealing process once drawed.
为了改善针布齿条淬火时的变形开裂倾向性,使其最终性能均匀,研究了针布齿条专用高碳低合金钢丝经过不同程度拉拔变形后,在相同球化退火工艺下具有差异的球化退火组织,并且比较了经较大拉拔变形后钢丝退火前后的组织差异,以及该钢丝经轧制前后的组织变化情况。
3) high strength medium carbon steel wire
高强度中碳钢丝
4) high carbide low alloy steel wire
高碳低合金钢钢丝
5) Low carbon steel wire
低碳钢丝
1.
To introduce natural aging of galvanized low carbon steel wire after softening treatment and effect of the aging on mechanical properties of steel wire.
介绍镀锌低碳钢丝经软化处理后产生的自然时效及其对钢丝力学性能的影响。
2.
To analyze the characteristics of the coal powder burning furnace The practice experiences of low carbon steel wire heat treatment with coal powder burning furnace are introduced Three pieces of norms about laying down the annealing technology of low carbon steel wire are pointed ou
分析燃煤粉炉的特点,介绍燃煤粉炉热处理低碳钢丝的实践经验,指出制定低碳钢丝退火工艺的3条准则。
3.
o introduce the drawing of low carbon steel wire without pickling and the keys to the technique.
介绍低碳钢丝无酸拉拔技术及无酸洗拉拔的技术关键，分析新工艺的优点，指出应进一步完善的技术要点。
补充资料：高碳钢
分子式：
CAS号：
性质：含碳量大于0.6％的碳素钢，常用含碳量为0.60％～1.50％。除碳外还可含有少量锰(0.70％～1.20％)，如65Mn。高碳钢都属于优质碳素钢或高级优质碳素钢，如T8A等。用高碳钢制成的各种零件，一般都必须经过不同形式的热处理后再使用。因为含碳量较高，热处理后可以较容易得到高强度(σb>980MPa)、高硬度(HRC60以上)以及优良的耐磨性，并具有一定的塑性和韧性。可作为工具钢及弹簧钢等使用。
CAS号：
性质：含碳量大于0.6％的碳素钢，常用含碳量为0.60％～1.50％。除碳外还可含有少量锰(0.70％～1.20％)，如65Mn。高碳钢都属于优质碳素钢或高级优质碳素钢，如T8A等。用高碳钢制成的各种零件，一般都必须经过不同形式的热处理后再使用。因为含碳量较高，热处理后可以较容易得到高强度(σb>980MPa)、高硬度(HRC60以上)以及优良的耐磨性，并具有一定的塑性和韧性。可作为工具钢及弹簧钢等使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。