1) medium-high carbon steel
中高碳钢
1.
The application of dynamic control with offgas analysis for making medium-high carbon steel on 95 t converter at Ma′anshan is presented.
介绍了马钢95 t转炉冶炼中高碳钢时,应用烟气分析动态控制炼钢技术,制定合适的装入、造渣、供氧制度,优化了造渣过程,提高了脱磷效率。
2.
This paper analyzes mainfactors that influence the dephosphorization of medium-high carbon steels in con-verter steelmaking process.
分析了转炉冶炼中高碳钢条件下影响脱磷的主要因素。
3.
The temperature and residual stress fields of medium-high carbon steel during following cooling process after hard-face-welding (hardfacing) with rare earth (RE) oxides were measured.
采用红外热像仪和X射线应力仪分别测定了采用含稀土氧化物的堆焊焊条,对中高碳钢试件进行堆焊过程的温度场和残余应力场,根据实验数据和材料的物理、力学参数,采用二维有限元计算方法,建立了堆焊应力场模型,根据这一模型,分析了马氏体相变对堆焊金属残余应力场的影响。
2) medium and high carbon steel
中、高碳钢
1.
Practice for Process of EAF Carbon Pick-up Operation for Production of Medium and High Carbon Steels;
EAF留碳操作生产中、高碳钢的工艺实践
2.
The medium and high carbon steels were quenched with and without magnetic field in the self-made quench tank,the austenite transformation in the NaCl solution was studied,and the microstructure change after phase transformation was observed.
利用自制的磁场热处理设备对中、高碳钢进行了施加磁场与不施加磁场的淬火处理,研究了奥氏体在NaCl溶液中冷却时的组织转变,观察了相变后的组织变化。
3) high carbon medium manganese steel
高碳中锰钢
1.
Effects of tempering temperature on high carbon medium manganese steel has been investigated in present work.
研究了回火温度对变质高碳中锰钢组织与性能的影响 ,结果表明 :随回火温度升高冲击韧度增大 ,组织中回火碳化物增多、耐磨性提高 ,当回火温度达 30 0℃时 ,无缺口冲击韧度达最大值 ,为 12 1。
4) medium-Carbon high-Manganese steel
中碳高锰钢
1.
LTD produce medium-Carbon high-Manganese steel.
本文根据迁钢公司板坯铸机生产中碳高锰钢的生产实践调查影响纵裂的因素,分析了纵裂发生的原因,通过采取一定的措施,使得中碳高锰钢的纵裂得到了控制。
5) high carbon medium-alloy steel
高碳中合金钢
1.
Transformation and morphology of carbides in high carbon medium-alloy steels during transforming process;
三种高碳中合金钢在热处理过程中的碳化物转变及形貌
2.
The investigation shows that M23C6 and M3C in Cr-W-Mo-V high carbon medium-alloy steels gradually dissolve into the matrix during heat process at about αγ temperature, and gradually precipitate again from the matrix during low cooling process.
研究表明,Cr-W-Mo-V高碳中合金钢加热至αγ温度区附近,M23C6和M3C会逐渐溶解于基体中,缓冷过程逐渐析出M23C6、M3C,并在αγ温度区发生M23C6M6C转变,而球状VC则变化不大,其碳化物超细化主要南溶解、形核的转变过程所引起的。
6) medium-high carbon Si-Mn steels
中高碳Si-Mn钢
补充资料：高碳钢
分子式：
CAS号：
性质：含碳量大于0.6％的碳素钢，常用含碳量为0.60％～1.50％。除碳外还可含有少量锰(0.70％～1.20％)，如65Mn。高碳钢都属于优质碳素钢或高级优质碳素钢，如T8A等。用高碳钢制成的各种零件，一般都必须经过不同形式的热处理后再使用。因为含碳量较高，热处理后可以较容易得到高强度(σb>980MPa)、高硬度(HRC60以上)以及优良的耐磨性，并具有一定的塑性和韧性。可作为工具钢及弹簧钢等使用。
CAS号：
性质：含碳量大于0.6％的碳素钢，常用含碳量为0.60％～1.50％。除碳外还可含有少量锰(0.70％～1.20％)，如65Mn。高碳钢都属于优质碳素钢或高级优质碳素钢，如T8A等。用高碳钢制成的各种零件，一般都必须经过不同形式的热处理后再使用。因为含碳量较高，热处理后可以较容易得到高强度(σb>980MPa)、高硬度(HRC60以上)以及优良的耐磨性，并具有一定的塑性和韧性。可作为工具钢及弹簧钢等使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。