2) Zn-bearing blast furnace dust
高炉含锌粉尘
3) zinc-bearing metallurgical dusts
含锌高炉粉尘
1.
The desulfurization using zinc-bearing metallurgical dusts from blast furnaces has been evaluated through measuring the change of SO2 content in flue gas generated from combusting coal powders.
研究了含锌高炉粉尘对燃煤产生的烟道气的脱硫行为。
4) Zinc-bearing Dust
含锌粉尘
1.
Desulfurization of high temperature coke oven gas (COG) by mixing zinc-bearing dust into coking coal has been studied.
提出了在炼焦过程中利用含锌粉尘作为焦煤添加剂,从而实现高温焦炉煤气脱硫的设想。
5) Zn-Pb-bearing dusts
含锌铅粉尘
1.
Therefore, the research on the treatment for Zn-Pb-bearing dusts has been one of the hotspots of the metallurgical field in recent years.
目前国内外处理工艺尚无法处理含铅高、含铁低的含锌铅粉尘。
6) EAF dust
电炉粉尘
1.
Simulation research on the EAF dust online recycling and zinc oxide separation with coke bed filter was carried out by heating coke/dust samples in CO/CO2 gas mixture.
采用电炉粉尘与焦炭粉的混合试样,对利用焦炭过滤床在线回收电炉粉尘,在CO/CO2混合气体中氧化锌的还原分离工艺进行了模拟研究。
2.
Using chemical reagent and EAF dust as experimental samples,the reduction of zinc oxide by solid carbon or CO/CO2 gas mixture was tested and the influence factors were analyzed.
用化学试剂和实际电炉粉尘作试样,考察了利用固体碳和CO/CO2进行氧化锌还原的各种影响因素。
3.
The Zn Pb containing EAF dust of Guanzhou Iron & Steel Works has been examined and analyzed and proposal is put forward that the EAF dust is used as the Fe containing corrective addition to produce cement,and feasibility tests have already been carried out.
对广州钢铁厂含铅锌电炉粉尘进行了分析测定,提出将电炉粉尘用作水泥生产铁质校正料的设想,并进行了可行性试验。
补充资料：含铁粉尘
钢铁生产过程中产生的粉尘或尘泥,如烧结粉尘,高炉煤气灰、泥，转炉尘泥和氧化铁皮等。在一般情况下，含铁粉尘和氧化铁皮量约占钢产量的 6～10％。粉尘大部分颗粒很细，常含有铅、锌和碱金属氧化物等有害杂质，要污染环境，应予回收利用。
钢铁厂通常回收的含铁粉尘的化学成分及粒度组成（％）例示如表。
通过除尘设施回收的含铁粉尘，需经造块，有些杂质,如ZnO等，也要在处理过程中排除，才能利用。其工艺主要有三：①金属化球团法。金属化率和脱锌率都在90％以上，可充分利用粉尘中的炭，燃料消耗较低。②烧结法。将脱锌后的高炉尘泥与转炉泥、烧结灰混合造球，作为烧结配料进入烧结机。烧结法流程简单，粉尘中所含的炭在烧结中得到利用，但脱锌率较低（75％）。③氧化球团法。企业设有球团厂,而粉尘含锌较低时,可作为球团原料使用。
钢铁厂通常回收的含铁粉尘的化学成分及粒度组成（％）例示如表。
通过除尘设施回收的含铁粉尘，需经造块，有些杂质,如ZnO等，也要在处理过程中排除，才能利用。其工艺主要有三：①金属化球团法。金属化率和脱锌率都在90％以上，可充分利用粉尘中的炭，燃料消耗较低。②烧结法。将脱锌后的高炉尘泥与转炉泥、烧结灰混合造球，作为烧结配料进入烧结机。烧结法流程简单，粉尘中所含的炭在烧结中得到利用，但脱锌率较低（75％）。③氧化球团法。企业设有球团厂,而粉尘含锌较低时,可作为球团原料使用。