1) Al2O3-ZrB2-C system
A12O3-ZrB2-C
2) ZrB2/C composite
ZrB2/C复合材料
1.
The mass and linear ablation rates of ZrB2/C composites prepared by hot-pressing method are tested in an oxyacetylene flame with high velocity gas.
采用热压法制备ZrB2/C复合材料,利用氧乙炔火焰烧蚀法测试材料的质量烧蚀率和线烧蚀率,采用扫描电镜和X射线衍射分析材料的微观结构及物相变化。
3) ZrO2-C-ZrB2 composites
ZrO2-C-ZrB2复合材料
1.
The oxidation kinetics of ZrO2-C-ZrB2 composites with 10% ZrB2 were investigated in the temperature range from 800 to 1100℃ in air by differential thermal analysis(DTA) and thermogravimetry(TG) techniques.
通过差热-热重分析研究了ZrB2含量为10%的ZrO2-C-ZrB2复合材料在800~1100℃下空气中的氧化动力学,根据气固相反应原理建立氧化动力学模型,计算反应表观活化能,并得到氧化速率与温度的经验关系式。
4) ZrB_2
ZrB2
1.
Through analyses by XRD it shows that Zr(CO_3)_2 and KBF_4 reactive products are ZrB_2,Al_2O_3,ZrAl_3 particles respectively, the reinforced particles of permanent mold casting composites are significantly larg.
采用熔体反应法,以Al Zr(CO3)2 KBF4反应体系原位反应合成颗粒增强铝基复合材料 用SEM分析生成的复合材料微观组织,用水淬快速冷却得到的增强相颗粒,尺寸细小并且在基体中分布均匀 XRD分析表明:Zr(CO3)2和KBF4与铝液反应生成ZrB2、Al2O3、ZrAl3颗粒,金属型复合材料的增强相颗粒尺寸显著增大,复合材料的拉伸强度和显微硬度随加入的反应物质量分数的增加而增大,但是延伸率先升后降,属塑性断
2.
Application of ZrB_2 in Inorganic Nonmetallic Materials;
ZrB2应用于复合材料中,能改善材料的机械性能、抗热震性能、抗氧化性能。
5) ZrB_2-SiC
ZrB2-SiC
1.
In this paper,the ZrB_2-SiC ceramic matrix composites were prepared by pressless sintering with YAG as sintering additive.
以钇铝石榴石-YAG为烧结助剂,通过无压烧结制备了ZrB2-SiC复相陶瓷。
2.
The oxidation resistance of ZrB_2-SiC composites prepared by heat-press sintering was studied using thermogravimetric analysis.
通过变温氧化增重试验和恒温氧化增重试验,研究了烧结温度对热压烧结制备的ZrB2-SiC复合材料的抗氧化性能的影响。
3.
ZrB_2-SiC composites were prepared by hot pressing sintering.
采用热压烧结法制备ZrB2-SiC复合材料。
6) NiP-ZrB_2
NiP-ZrB2
补充资料：zirconium boride (zrb2) zirconium boride Zirconium boride(ZrB2)
CAS：12045-64-6
分子式：ZrB2
分子质量：112.84
中文名称：硼化锆
英文名称：zirconium boride (zrb2) zirconium boride Zirconium boride(ZrB2)
分子式：ZrB2
分子质量：112.84
中文名称：硼化锆
英文名称：zirconium boride (zrb2) zirconium boride Zirconium boride(ZrB2)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条