Microstructure and mechanical properties of the in-situ synthesized A356/TiB_2 composites have been investigated.
对原位反应合成TiB2/A356铝基复合材料微观组织和力学拉伸性能进行了研究。
2.
The ceramic composites TiB_2-TiN-(Ni,Mo) with different contents of TiN were fabricated by hot press technology and the mechanical properties were measured.
热压烧结制备了不同TiN含量的复合陶瓷刀具材料TiB2-TiN-(Ni,Mo),对其性能测试表明,随着TiN含量的增加,材料的抗弯强度和断裂韧度逐渐提高,但是材料的硬度在TiN的含量达到40%(体积分数)时却大幅度降低。
3.
TiB_2/B_4C composite ceramic powder was synthesized in situ through co-precipitation mainly with TiCl_4 solution and B_4C powder as raw materials.
采用共沉淀技术,以TiCl4溶液和B4C粉末为主要原料原位合成了TiB2/B4C陶瓷复合粉体。
3) TiB 2
TiB2
1.
Ni-TiB 2 ceramic-metal composite coating is cladded on the surface of 45# steel by CO 2 laser melting a precursor mixture of nickel based alloy powder,boron and titanium powders.
利用激光熔覆技术,使用HL 1500型CO2 激光器在 45#钢表面制备出原位自生成的Ni基金属陶瓷TiB2 涂层。
2.
The synthesis reaction mechanism of TiB 2 during mechanical alloying was also discussed.
采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)及粉体粒度仪研究了Ti33B6 7元素混合粉在机械合金化过程中的结构演变、球磨后粉体的颗粒形态与粒度分布以及热处理对粉体结构的影响,讨论了TiB2 机械合金化合成机制。
3.
Calculating of ΔG T of laser cladding composite coating reaction system shows that TiB 2 is most possibly fabricated, and XRD analysis proves it too.
对激光熔覆复合涂层反应体系标准反应吉布斯自由能 (ΔGT)的计算表明 :TiB2 生成的可能性最大 ,XRD分析也证明了这一点。
4) TiB2 inert cathode
TiB2惰性阴极
5) TiB_2 powders
TiB2粉
6) TiB_2/BN
TiB2/BN
补充资料：3D特性
翻译为：AlphaBlending(α混合) 简单地说这是一种让3D物件产生透明感的技术。屏幕上显示的3D物件，每个像素中有红、绿、蓝三组数值。若3D环境中允许像素能拥有一组α值，我们就称它拥有一个α通道。α值的内容，是记载像素的透明度。这样一来使得每一个物件都可以拥有不同的透明程度。比如说，玻璃会拥有很高的透明度，而一块木头可能就没什么透明度可言。α混合这个功能，就是处理两个物件在萤幕画面上叠加的时候，还会将α值列入考虑，使其呈现接近真实物件的效果。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条