2) Water soluble resin
水溶性树脂
1.
Water soluble resin has been proved by experiment in lab to be capable of replacing synthetic grease or Chinese wood oil in foundry production so as to lower core gas generation and shorten generation time resulting in both dramatic reduction of waster caused by blowhole and effective improvement on working environment.
经实验室试验及生产验证,水溶性树脂可代替合脂油及桐油应用于铸造生产中,从而降低了砂芯的发气量,缩短了发气时间,使铸件的气孔废品率大幅度下降,并且可以有效地改善工人的作业环境。
3) water-soluble epoxy resin
水溶性环氧树脂
1.
Crosslinking anionic emulsion was formed based on the emulsion and water-soluble epoxy resin.
采用种子聚合制备了丙烯酸系乳液,在此基础上配合水溶性环氧树脂,形成交联型阴离子乳液。
4) water soluble phenol-formaldehyde resin
水溶性酚醛树脂
1.
Synthesis the water soluble phenol-formaldehyde resin by two step alkaline catalytic reaction;
两步碱催化法合成水溶性酚醛树脂
2.
Activated carbon prepared from water soluble phenol-formaldehyde resin for application in supercapacitor;
水溶性酚醛树脂制备超级电容器用活性炭
3.
Stability of dilute water soluble phenol-formaldehyde resin solution;
水溶性酚醛树脂稀溶液的稳定性
5) water-soluble alkyd resin
水溶性醇酸树脂
1.
A two-component waterborne polyurethane coatings is composed of part A formulated by water-soluble alkyd resin,pigments,fillers and additives,and part B containing modified hydrophilic polyisocyanate.
采用水溶性醇酸树脂、颜填料及助剂制备A组分,同亲水改性多异氰酸酯配合(B组分),制备双组分水性聚氨酯工业涂料。
2.
The synthesis of water-soluble alkyd resin by modified resin and preparation of priming paint were studied.
产物的耐热性表明,其具有良好的耐热性,用改性松香类水溶性醇酸树脂制备的底漆具有较好的性能。
3.
A general program of formulating of recipe suitable for self-drying water-soluble alkyd resin was established.
建立了适合于水溶性醇酸树脂配方设计的通用程序。
6) water soluble phenolic resin
水溶性酚醛树脂
1.
Weaving frictional material,soaked by water soluble phenolic resin,is tested by the DMS-1 constant speed friction and wear tester according to the standard of GB/T11834-2000.
研究了不同含碱量的水溶性酚醛树脂对摩擦材料性能的影响。
补充资料：水溶性树脂
分子式：
分子量：
CAS号：
性质：能溶于水的树脂。主要有：（1）低分子量的脲醛树脂和三聚氰胺甲醛树脂，可用作纺织品防皱防缩处理剂、胶粘剂、涂料等；（2）甲阶段酚醛树脂，可用作鞣革剂和胶粘剂等；（3）聚丙烯酸或聚甲基丙烯酸的盐类，可用作纺织品上浆剂或增稠剂，聚丙烯酸钙可以改善飞机场跑道等的路面；（4）聚乙烯醇，可用作纸张的着色涂料、防油涂料、分散剂、胶粘剂、聚酰胺纤维的浆料，塑化聚乙烯醇可挤压成耐油脂、耐有机溶剂的管材和片材；（5）聚环氧乙烷，溶于水后生成粘性液体，可用作乳化剂和增稠剂、胶粘剂的膏料等，也可用作包装农药、墨水粉、洗涤剂等的薄膜，以便于溶在水中使用；（6）聚N-乙烯基吡咯烷酮，可配成水溶液，经药物处理后作血浆代用品，治疗水肿病的药剂；（7）含有自由基的醇酸树脂，可用氨水或胺类处理成水溶性铵盐，用于制电泳漆。
分子量：
CAS号：
性质：能溶于水的树脂。主要有：（1）低分子量的脲醛树脂和三聚氰胺甲醛树脂，可用作纺织品防皱防缩处理剂、胶粘剂、涂料等；（2）甲阶段酚醛树脂，可用作鞣革剂和胶粘剂等；（3）聚丙烯酸或聚甲基丙烯酸的盐类，可用作纺织品上浆剂或增稠剂，聚丙烯酸钙可以改善飞机场跑道等的路面；（4）聚乙烯醇，可用作纸张的着色涂料、防油涂料、分散剂、胶粘剂、聚酰胺纤维的浆料，塑化聚乙烯醇可挤压成耐油脂、耐有机溶剂的管材和片材；（5）聚环氧乙烷，溶于水后生成粘性液体，可用作乳化剂和增稠剂、胶粘剂的膏料等，也可用作包装农药、墨水粉、洗涤剂等的薄膜，以便于溶在水中使用；（6）聚N-乙烯基吡咯烷酮，可配成水溶液，经药物处理后作血浆代用品，治疗水肿病的药剂；（7）含有自由基的醇酸树脂，可用氨水或胺类处理成水溶性铵盐，用于制电泳漆。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。