1) Al electroplating in melted salt bath at ambient temperature
室温熔盐电镀铝
2) ambient temperature chloroaluminate melts plating
室温熔盐电镀
5) room temperature molten salt
室温熔盐
1.
Application of room temperature molten salt as electrolyte for electrochemical capacitor based on carbon nanotube;
室温熔盐在碳纳米管电化学电容器中的应用
2.
Capacitance characteristics of activated carbon in room temperature molten salt electrolyte
活性炭在室温熔盐电解质中的电容特性
3.
Two concepts,the window of room temperature molten salt (RTMS) and depth of RTMS,were given to represent the capability and property of R.
在充有高纯氮气的干燥手套箱内,将硝酸铵和乙酰胺+尿素混合,用称重法准确配制含不同硝酸铵摩尔分数的硝酸铵和乙酰胺+尿素混合样品,利用差示扫描量热法建立了硝酸铵和乙酰胺+尿素二元相图·提出了室温熔盐窗口和室温熔盐深度两个概念,用来衡量形成室温熔盐的能力及其性质·依据相图,指出了该体系能形成室温熔盐,室温熔盐窗口的组成范围是x(NH4NO3)=15%～40%;室温熔盐深度为32K
6) room temperature molten salts
室温熔盐
1.
Electrodeposition of aluminum on stainless steel from room temperature molten salts
不锈钢基体室温熔盐电沉积铝
2.
Influence of acid pickling on electrodeposition of aluminum on magnesium alloy in room temperature molten salts
酸浸蚀处理对AZ91D镁合金室温熔盐镀铝的影响
3.
At first, the dense, uniform aluminum coating was electrodeposited on 201 austenitic stainless steel from acid AlCl_3-EMIC (2∶1) room temperature molten salts, then the samples were heat treated for 2min～100h at 570℃～680℃.
本研究以201奥氏体不锈钢为基体,在酸性的AlCl3-EMIC(2∶1)室温熔盐中电沉积均匀致密的铝镀层,然后在570℃～680℃下对试样进行2min～100h的热处理,用SEM、EDS及XRD对热处理后的试样界面进行微观分析。
补充资料：熔盐电镀
分子式：
CAS号：
性质：以熔盐电解法在材料或工件表面形成防护层或其他功能层的一种方法。熔盐电镀可消除电镀氢脆，在炮管熔盐镀铬和在高强度材料电镀上特别重要。熔盐电镀通常有较好的结合力，因为镀层与基体可能形成中间合金。熔盐电镀中难以应用有机络合剂、光亮剂等，使镀层品质控制常常发生困难。熔盐电镀通常需要惰性保护气氛，这样装置复杂、操作困难、规模难以扩大。成本过高使熔盐电镀仅局限于一些特殊场合。
CAS号：
性质：以熔盐电解法在材料或工件表面形成防护层或其他功能层的一种方法。熔盐电镀可消除电镀氢脆，在炮管熔盐镀铬和在高强度材料电镀上特别重要。熔盐电镀通常有较好的结合力，因为镀层与基体可能形成中间合金。熔盐电镀中难以应用有机络合剂、光亮剂等，使镀层品质控制常常发生困难。熔盐电镀通常需要惰性保护气氛，这样装置复杂、操作困难、规模难以扩大。成本过高使熔盐电镀仅局限于一些特殊场合。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。