1) plating on aluminium
铝上电镀
2) Ni plating on Al alloy
铝上镀镍
3) aluminized coat
镀铝上衣
4) electrodeposition aluminum
电镀铝
1.
The feasibility of electrodeposition aluminum on 304 stainless steel from AlC1_3-NaCl-KCl inorganic molten salts was studied.
在AlC13-NaCl-KCl三元无机熔融盐体系中研究了304不锈钢基体上熔融盐电镀铝的可能性,并对镀层的形貌和成分进行了分析。
5) electroplating aluminum coating
电镀铝
1.
Influence of anodic-oxidation-process on microstructure and properties of electroplating aluminum coating on the steel;
钢基电镀铝层阳极氧化处理后的组织结构和性能
2.
The microstructure and morphology of electroplating aluminum coating on Q235 steel after being anodically oxidized in sulfuric acid solution for different time were investigated by means of SEM and XRD,and the hardness and corrosion resistance of the treated aluminum coating was also examined.
用扫描电镜(SEM)和 X 射线衍射分析(XRD)测定了 Q235钢上电镀铝层在硫酸溶液中不同时间阳极氧化处理后的组织结构和表面形貌,并对其硬度和耐蚀性能进行了测试。
6) electroplating aluminum
电镀铝
1.
Influence of micro-arc oxidation process on phase structure and properties of electroplating aluminum coating on Q235 steel;
微弧氧化处理对Q235钢电镀铝层相结构和性能的影响
2.
The electroplating aluminum on Q235 steel has been realized and obtained a certainty plating layer at 150℃ and 800℃ respectively in molten salts of AlCl3-NaCl-KCl and NaCl-KCl.
本研究用AlCl_3-NaCl-KCl和NaCl-KC1两种熔融盐分别于150℃和800℃实验条件下在Q235钢基体上得到了一定厚度的电镀铝层。
补充资料：铝和铝合金电镀
分子式：
分子量：
CAS号：
性质：纯铝具有较好的耐蚀性，但机械强度差，一些铝合金机械强度虽高，却耐热性、耐磨性差、接触电阻大和装饰性不佳等缺点。为改善其表面状态，必须进行表面处理。例如铝件镀或银，可改善其导电性；铝件镀铬，可增加表面硬度和耐磨性，并获得良好的装饰外观；铝件镀锡合金，可提高焊接性和减磨性等。在铝上进行电镀必须采取特殊的前处理工艺。一般经浸锌处理，铝表面的氧化膜被锌代替，就可电镀其他金属。
分子量：
CAS号：
性质：纯铝具有较好的耐蚀性，但机械强度差，一些铝合金机械强度虽高，却耐热性、耐磨性差、接触电阻大和装饰性不佳等缺点。为改善其表面状态，必须进行表面处理。例如铝件镀或银，可改善其导电性；铝件镀铬，可增加表面硬度和耐磨性，并获得良好的装饰外观；铝件镀锡合金，可提高焊接性和减磨性等。在铝上进行电镀必须采取特殊的前处理工艺。一般经浸锌处理，铝表面的氧化膜被锌代替，就可电镀其他金属。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。