1) ESCC
电渣连铸
1.
The factors affecting internal quality of billets were analyzed and the analysis of macrostructure,microstructure and inclusion were made on the 90 mm×90 mm remelted billets produced by the electroslag continuous casting(ESCC)under the condition of voltage 60 V and current 3 400~4 200 A.
介绍了电渣连铸坯内部质量控制理论,并对在电压60 V、电流3 400～4 200 A供电参数下生产的90 mm×90 mm电渣连铸小方坯进行了低倍、高倍、夹杂物等检验分析。
2.
The factors affecting internal quality of billets were analyzed and the analysis of macrostructure,microstructure and inclusion were made on the 90mm×90mm remelted billets produced by the electroslag continuous casting(ESCC) under the condition of voltage 60V and current 3400～4200A.
对电渣连铸坯内部质量控制理论基础进行了分析,并对在电压60V、电流3400～4200A 供电参数下生产的90mm×90mm 电渣连铸小方坯进行了低倍、高倍、夹杂物等检验分析。
2) electroslag continuous casting
电渣连铸
1.
Basing on each features of ESR and CC,the electroslag continuous casting(ESCC) process was developed successfully firstly in Northeastern University by adopting the technologies of double electrodes in series,alternative electrodes and truncation on-line.
在结合电渣重熔和连铸技术优点的基础上,东北大学钢铁冶金研究所采用双极串联、交换电极及在线切割等技术,在国内首次成功地开发了电渣连铸(ESCC)技术;解决了电渣重熔钢锭直径小于300 mm时熔速很慢、冶炼费用很高的难题。
3) ESR Continuous Casting Ingot
电渣连铸锭
4) mold fluxes
连铸保护渣
1.
Discuss on quality evaluation system of continuous casting mold fluxes;
连铸保护渣质量评价体系探讨
2.
Development of mold fluxes for welding rod steel at the Shuicheng Iron and Steel(Group) Co., Ltd.
水钢H08钢连铸保护渣的研制
3.
Effects of titania (TiO2) on viscous characteristics of mold fluxes (MF) for stainless steel were investigated by rotary viscometry, transmission electron microscope and X-ray diffraction.
采用旋转黏度计并借助岩相分析系统探讨了二氧化钛(TiO2)对不锈钢连铸保护渣(moldfluxes,MF)黏性特征影响的作用机制。
5) mold powder
连铸保护渣
1.
Effect of atmosphere and addition agent on the melting rate of low carbon mold powder in continuous casting;
气氛和添加剂对低碳连铸保护渣熔速的影响
2.
Crystallization temperature of mold powder was measured by DTA.
利用差热分析仪,研究连铸保护渣的结晶温度与碱度、Na2CO3含量、CaF2含量、Al2O3含量和MgO含量之间的关系,进而通过建立非线性规划模型,对连铸保护渣的结晶性能进行优化设计和模型预测。
3.
Under the present experimental conditions,the viscosity,solidification temperature and activation energy of mold powder all decrease with increasing BI and,meanwhile,the effect of BI on viscous characteristics of mold powder gradually weakens.
利用旋转黏度计,全面研究连铸保护渣的黏度、凝固温度和黏性活化能与碱度、综合碱度之间的关系。
6) CC mold flux
连铸保护渣
1.
The melting speed of low carbon CC mold flux composed of different carbon materials(graphite and active carbon) and different carbon mass fraction((2.
2%)的低碳连铸保护渣在空气中和在氩气中的熔化速度,结果是在有惰性气体保护下的熔化速度远小于一般在空气中的熔化速度。