1)  remained heat treatment
余热处理
1.
Finite element simulation for the remained heat treatment of large gauge ribbed bar;
大规格带肋钢筋余热处理过程的有限元模拟
2.
The results show that BS 460MPa grade reinforced bar can be produced all from Q235 or 20MnSi billet by the remained heat treatment process but the production cost of the former is lower.
以Q235、20MnSi钢坯为原料进行了用余热处理工艺生产英标460MPa级钢筋的试验,研究了水冷段数、水压、上冷床温度以及成分、钢种和时效对钢筋性能的影响。
2)  residual heat treatment
余热处理
1.
The qualified reinforced bar is produced by designing chemical composition and developing QTB residual heat treatment process.
介绍了英标460B钢筋的研制情况,通过成分设计和开发QTB余热处理工艺生产出合格的钢筋。
2.
In order to resolve the pr oblem of ribbed bar rust after rol ling,the technology of residual heat treatment was applied,which realized by water cooling after rolling The mechanis m of the technology,the obvious ef fects and benefits were introduce
莱芜钢铁集团公司为解决带肋钢筋轧后锈蚀问题对其进行余热处理 ,通过轧后穿水实施在线高温阻锈技术。
3)  heat treatment with residual rolling temperature
余热热处理
1.
The results indicted that the better resistance to impact fracture for the test grinding balls could be obtained by making use of a given heat treatment with residual rolling temperature.
结果表明 ,该球经适当的轧后余热热处理可获得较高的抗多冲击破坏能
2.
The abrasiveness of cross rolled low chromium white cast iron grinding ball has been studiedthroug the test of abrasion,and the characters of abrasion surface was analyzed,The results show that the better vesistance to abrasion for the test grinding balls could be obtained by Making use of a given heat treatment with residual rolling temperature.
结果表明 :斜轧低铬白口铸铁磨球经适当的余热热处理可获得较高的耐磨性
4)  Casting remained heat treatment
铸造余热热处理
5)  heat treating with the residual heat after hot rolling
轧后余热热处理
1.
The result showed that mechanical properties of the bar was increased by heat treating with the residual heat after hot rolling,and could be satisfied with the requirements of standard YB13 - 69.
对16Mn钢筋轧后余热热处理工艺进行了试验,结果表明,经轧后余热热处理的钢筋,其力学性能得以提高,可满足YB13—69标准的要求。
6)  remained heat treatment after rolling
轧后余热处理
1.
Through making technological condition and process flow,Laiwu steel developed BS 460B Φ50 mm concrete reinforcement steel by VN micro-alloying and remained heat treatment after rolling.
莱钢通过制定试制产品的技术条件和工艺流程,采用VN微合金化技术和轧后余热处理两种工艺,开发出了英标460BΦ50 mm钢筋混凝土用钢筋。
补充资料:表面处理、热处理关连用语英汉对照

age hardening 时效硬化 ageing 老化处理
air hardening 气体硬化 air patenting 空气韧化
annealing 退火 anode effect 阳极效应
anodizing 阳极氧化处理 atomloy treatment 阿托木洛伊表面
austempering 奥氏体等温淬火 austenite 奥斯田体/奥氏体
bainite 贝氏体 banded structure 条纹状组织
barrel plating 滚镀 barrel tumbling 滚筒打光
blackening 染黑法 blue shortness 青熟脆性
bonderizing 磷酸盐皮膜处理 box annealing 箱型退火
box carburizing 封箱渗碳 bright electroplating 辉面电镀
bright heat treatment 光辉热处理 bypass heat treatment 旁路热处理
carbide 炭化物 carburized case depth 浸碳硬化深层
carburizing 渗碳 cementite 炭化铁
chemical plating 化学电镀 chemical vapor deposition 化学蒸镀
coarsening 结晶粒粗大化 coating 涂布被覆
cold shortness 低温脆性 comemtite 渗碳体
controlled atmosphere 大气热处理 corner effect 锐角效应
creeping discharge 蠕缓放电 decarburization 脱碳处理
decarburizing 脱碳退火 depth of hardening 硬化深层
diffusion 扩散 diffusion annealing 扩散退火
electrolytic hardening 电解淬火 embossing 压花
etching 表面蚀刻 ferrite 肥粒铁
first stage annealing 第一段退火 flame hardening 火焰硬化
flame treatment 火焰处理 full annealing 完全退火
gaseous cyaniding 气体氧化法 globular cementite 球状炭化铁
grain size 结晶粒度 granolite treatment 磷酸溶液热处理
graphitizing 石墨退火 hardenability 硬化性
hardenability curve 硬化性曲线 hardening 硬化
heat treatment 热处理 hot bath quenching 热浴淬火
hot dipping 热浸镀 induction hardening 高周波硬化
ion carbonitriding 离子渗碳氮化 ion carburizing 离子渗碳处理
ion plating 离子电镀 isothermal annealing 等温退火
liquid honing 液体喷砂法 low temperature annealing 低温退火
malleablizing 可锻化退火 martempering 麻回火处理
martensite 马氏体/硬化铁炭
metallikon 金属喷镀法
metallizing 真空涂膜 nitriding 氮化处理


~

nitrocarburizing 软氮化 normalizing 正常化
oil quenching 油淬化 overageing 过老化
overheating 过热 pearlite 针尖组织
phosphating 磷酸盐皮膜处理 physical vapor deposition 物理蒸镀

说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条