1) calcium sulfate anhydrate
无水硫酸钙
1.
The effects of different amounts of calcium sulfate anhydrate and different liquid for hardening on the microstructure,the setting time,compressive strength and phase composition of the CSA/α-TCP bone cement were investigated.
研究了无水硫酸钙(CSA)及不同固化液对α-磷酸三钙(α-TCP)体系骨水泥的显微结构、固化时间、力学强度及物相组成等的影响。
2.
The calcium phosphate bone cement was prepared by the introduction of calcium sulfate anhydrate (CSA),the effects of which on the structure and performance of α-tricalcium phosphate bone cement was investigated by means of the thermal analysis,scanning electric microscopy,mechanics performance testing as well as comparative experiments.
将无水硫酸钙(CSA)引入磷酸钙骨水泥(CPC)中,结合热分析(TG-DSC)、扫描电子显微分析(SEM)和力学性能测试等方法,通过对比试验研究了CSA对α-磷酸三钙(α-TCP)体系骨水泥结构与性能的影响。
3.
The effects of different amounts of calcium sulfate anhydrate on t.
无水硫酸钙(CSA)是一种生物相容性好,可降解的潜在的生物材料,本课题首次将CSA引入CPC中,研究了CSA对α—TCP体系骨水泥性能的影响,实验结果表明适量CSA的加入可促进骨水泥的固化,使得固化产物的长径比增加从而提高了固化体的抗压强度。
2) calcium sulphoaluminate
无水硫铝酸钙
1.
Under the process conditions,qualified sulphoaluminate cement clinker can be produced and main mineral composition of cement clinker are calcium sulphoaluminate and dicalcium silicate.
结果表明:用本试验所采用的原料,配料比为m(矾土)∶m(石灰石)∶m(脱硫石膏)=35∶43∶22,煅烧温度为1400℃可烧制成矿物组成为无水硫铝酸钙和硅酸二钙的合格硫铝酸盐水泥熟料。
3) C 4A 3S
无水硫铝酸钙
1.
The influence of P 2O 5 on the formation and hydration properties of C 4A 3S has been studied in this paper.
研究了掺杂P2 O5 对无水硫铝酸钙矿物形成及水化性能的影响。
4) calcium sulphate dihydrate
二水硫酸钙
1.
calcium sulphate dihydrate) were studied.
对影响钙离子向硫酸钙转化的各种因素及反应后产物二水硫酸钙的纯化处理进行了研究。
5) dihydrate calcium sulphate
二水硫酸钙
1.
Research progress on the crystallization course of dihydrate calcium sulphate;
二水硫酸钙结晶过程研究进展
2.
Study on the crystallization course of dihydrate calcium sulphate and the effect of APA on its crystallization;
二水硫酸钙结晶过程及活化疏松剂对其影响的研究
6) CaSO 4·2H 2O
二水硫酸钙
1.
The crystal growth phenomenon of CaSO 4·2H 2O and the effects of different inorganic substances as additives on it in the stable supersaturated solution.
本文主要研究二水硫酸钙在稳定过饱和溶液 (Ca2 +浓度为 0 。
补充资料：十水硫酸钠
Na2SO4·10H20 分子量322.19
性状 无色单斜晶系结晶体或粉末。有苦咸味。100℃时失去结晶水。在空气中迅速风化而变为白色粉末无水物。溶于水、甘油，不溶于乙醇，水溶液呈中性。
应用领域 主要用于制备无水硫酸钠。也用于硫化钠、硅酸钠、群青等化工产品的生产。造纸工业用于制造硫酸盐纸浆，玻璃工业用于代替纯碱，染料工业中用作填充剂，印染工业用作助染剂。
性状 无色单斜晶系结晶体或粉末。有苦咸味。100℃时失去结晶水。在空气中迅速风化而变为白色粉末无水物。溶于水、甘油，不溶于乙醇，水溶液呈中性。
应用领域 主要用于制备无水硫酸钠。也用于硫化钠、硅酸钠、群青等化工产品的生产。造纸工业用于制造硫酸盐纸浆，玻璃工业用于代替纯碱，染料工业中用作填充剂，印染工业用作助染剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。