2) Hemihydrate calcium sulfate whiskers
半水硫酸钙晶须
4) α-Calcium sulphate hemihydrate
α型半水硫酸钙
5) calcium sulphate dihydrate
二水硫酸钙
1.
calcium sulphate dihydrate) were studied.
对影响钙离子向硫酸钙转化的各种因素及反应后产物二水硫酸钙的纯化处理进行了研究。
6) calcium sulfate anhydrate
无水硫酸钙
1.
The effects of different amounts of calcium sulfate anhydrate and different liquid for hardening on the microstructure,the setting time,compressive strength and phase composition of the CSA/α-TCP bone cement were investigated.
研究了无水硫酸钙(CSA)及不同固化液对α-磷酸三钙(α-TCP)体系骨水泥的显微结构、固化时间、力学强度及物相组成等的影响。
2.
The calcium phosphate bone cement was prepared by the introduction of calcium sulfate anhydrate (CSA),the effects of which on the structure and performance of α-tricalcium phosphate bone cement was investigated by means of the thermal analysis,scanning electric microscopy,mechanics performance testing as well as comparative experiments.
将无水硫酸钙(CSA)引入磷酸钙骨水泥(CPC)中,结合热分析(TG-DSC)、扫描电子显微分析(SEM)和力学性能测试等方法,通过对比试验研究了CSA对α-磷酸三钙(α-TCP)体系骨水泥结构与性能的影响。
3.
The effects of different amounts of calcium sulfate anhydrate on t.
无水硫酸钙(CSA)是一种生物相容性好,可降解的潜在的生物材料,本课题首次将CSA引入CPC中,研究了CSA对α—TCP体系骨水泥性能的影响,实验结果表明适量CSA的加入可促进骨水泥的固化,使得固化产物的长径比增加从而提高了固化体的抗压强度。
补充资料：半水硫酸钙
分子式：t1CaSO4•1/2H2O
CAS号：
性质： 白色粉末。在163℃失去结晶水变成无水物。溶于酸、铵盐、硫代硫酸钠和甘油，微溶于水。与水混合后形成塑性易浇砌浆体，隔一定时间后硬化成坚固石状体，并伴有微量的体积膨胀及放热。属于气硬性建筑胶凝物质。分α型和β型两种。α型俗称高强度建筑石膏，β型俗称熟石膏(plasterof paris)或烧石膏(burnt plaster；calcined gypsum)。由生石膏经粉碎至一定细度后加入高压釜，用蒸汽加压蒸煮，干燥、粉碎制得α型。由生石膏经粉碎、煅烧、粉碎、筛选后制得β型。α型用作建筑上高强度石膏构件、石膏板，铸造模型及机械加工时的固定胶凝加工件。β型用作建筑材料，粉饰石膏构件，石膏塑像，陶瓷器造型，雕塑模型，粉笔及作为胶凝剂、固定剂、牙科医疗材料等。
CAS号：
性质： 白色粉末。在163℃失去结晶水变成无水物。溶于酸、铵盐、硫代硫酸钠和甘油，微溶于水。与水混合后形成塑性易浇砌浆体，隔一定时间后硬化成坚固石状体，并伴有微量的体积膨胀及放热。属于气硬性建筑胶凝物质。分α型和β型两种。α型俗称高强度建筑石膏，β型俗称熟石膏(plasterof paris)或烧石膏(burnt plaster；calcined gypsum)。由生石膏经粉碎至一定细度后加入高压釜，用蒸汽加压蒸煮，干燥、粉碎制得α型。由生石膏经粉碎、煅烧、粉碎、筛选后制得β型。α型用作建筑上高强度石膏构件、石膏板，铸造模型及机械加工时的固定胶凝加工件。β型用作建筑材料，粉饰石膏构件，石膏塑像，陶瓷器造型，雕塑模型，粉笔及作为胶凝剂、固定剂、牙科医疗材料等。