2) calcium sulfate anhydrate
无水硫酸钙
1.
The effects of different amounts of calcium sulfate anhydrate and different liquid for hardening on the microstructure,the setting time,compressive strength and phase composition of the CSA/α-TCP bone cement were investigated.
研究了无水硫酸钙(CSA)及不同固化液对α-磷酸三钙(α-TCP)体系骨水泥的显微结构、固化时间、力学强度及物相组成等的影响。
2.
The calcium phosphate bone cement was prepared by the introduction of calcium sulfate anhydrate (CSA),the effects of which on the structure and performance of α-tricalcium phosphate bone cement was investigated by means of the thermal analysis,scanning electric microscopy,mechanics performance testing as well as comparative experiments.
将无水硫酸钙(CSA)引入磷酸钙骨水泥(CPC)中,结合热分析(TG-DSC)、扫描电子显微分析(SEM)和力学性能测试等方法,通过对比试验研究了CSA对α-磷酸三钙(α-TCP)体系骨水泥结构与性能的影响。
3.
The effects of different amounts of calcium sulfate anhydrate on t.
无水硫酸钙(CSA)是一种生物相容性好,可降解的潜在的生物材料,本课题首次将CSA引入CPC中,研究了CSA对α—TCP体系骨水泥性能的影响,实验结果表明适量CSA的加入可促进骨水泥的固化,使得固化产物的长径比增加从而提高了固化体的抗压强度。
3) anhydrous sodium sulfate
无水硫酸钠
1.
Then the anhydrous sodium sulfate is obtained after separating,wahsing and drying.
35g/cm3后析出Na2SO4晶体,经分离、洗涤、干燥后得无水硫酸钠产品。
2.
Aim\ The technological condition required to get anhydrous sodium sulfate from the industrial coarse mirabilite is discussed.
目的 研究用 DTB型结晶器从工业粗制芒硝中制取无水硫酸钠的工艺条件 。
3.
As the by-product the anhydrous sodium sulfate was obtained at the same time.
以硫氢化钠与运城盐湖的高镁卤水为原料,制取高纯氧化镁,并副产无水硫酸钠,为运城盐湖资源的综合利用提供了新思路。
4) anhydrous cupric sulfate
无水硫酸铜
1.
The hexadecanol bischloroacetate was synthesized fastly with the technique of microwave irradiation with the anhydrous cupric sulfate as catalyst.
研究了在无水硫酸铜的催化下,利用微波辐射技术快速合成氯乙酸十六酯的方法及影响反应收率的因素。
2.
DOF was prepared by using anhydrous cupric sulfate as an esterification catalyst of fumaric acid with isooctyl alcohol.
探讨了无水硫酸铜作催化剂合成富马酸二异辛酯的方法和工艺条件。
5) anhydrous Magnesium sulfate
无水硫酸镁
1.
In the presence of anhydrous Magnesium sulfate, lead Carbon dioxide to reactions of pyrrole and benzaldehydes ,direct condensation of pyrrole with benzaldehydes in refuxing DMF or DMSO gave TPPH2,The product will not contain meso-tetraphenylchlorin.
以N,N 二甲基甲酰胺或二甲基亚砜为溶剂,在无水硫酸镁存在下,将CO2通入吡咯与苯甲醛混合液中反应,可以直接合成不含四苯基二氢卟啉(简称TPC)的四苯基卟啉(简称TPPH2)。
6) anhydrous ironic sulfate
无水硫酸铁
1.
The desiccating ability of anhydrous ironic sulfate is better than that of anhydrous magnesium sulfate.
无水硫酸铁的干燥强度优于无水硫酸镁 ;干燥容量大大超过硅胶 ,是很值得开发的一种无机盐干燥剂 。
补充资料：十水硫酸钠
Na2SO4·10H20 分子量322.19
性状 无色单斜晶系结晶体或粉末。有苦咸味。100℃时失去结晶水。在空气中迅速风化而变为白色粉末无水物。溶于水、甘油，不溶于乙醇，水溶液呈中性。
应用领域 主要用于制备无水硫酸钠。也用于硫化钠、硅酸钠、群青等化工产品的生产。造纸工业用于制造硫酸盐纸浆，玻璃工业用于代替纯碱，染料工业中用作填充剂，印染工业用作助染剂。
性状 无色单斜晶系结晶体或粉末。有苦咸味。100℃时失去结晶水。在空气中迅速风化而变为白色粉末无水物。溶于水、甘油，不溶于乙醇，水溶液呈中性。
应用领域 主要用于制备无水硫酸钠。也用于硫化钠、硅酸钠、群青等化工产品的生产。造纸工业用于制造硫酸盐纸浆，玻璃工业用于代替纯碱，染料工业中用作填充剂，印染工业用作助染剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条