1) 20 dual-phase steel wire
20双相钢丝
2) 20 dual-phase steel
20双相钢
1.
The effects of high temperature deformation quenching and deformation magnitude on grain size and martensite shape of 20 dual-phase steel are discussed by microstructure observation and analysis.
通过组织观察分析,探讨高温形变淬火及形变量对20双相钢晶粒大小及马氏体形态的影响,实验表明当形变量超过50％时,双相组织明显细化,随着晶粒的细化,板条马氏体的尺寸减小,片状马氏体片长明显减小,片宽变化不大。
3) dual-phase steel wire
双相钢丝
1.
Microstructure and properties of dual-phase steel wire were studied.
对20双相钢丝的组织与性能进行了研究。
2.
This paper studies forming situation of texture of low carbon dual-phase steel wire indeep drawing.
本文中研究了低碳双相钢丝在深度拉拔过程中织构的形成情况 ,结果表明 :与较低温度 (740℃ )亚温淬火时相比 ,在较高温度 (如 840℃ )的亚温淬火使钢丝的织构发展得比较充
4) dual phase steel wire
双相钢丝
1.
A study has been made on the variation of elongation in 20 cold-drawn dual phase steel wire during the tempering at 500℃ for various times.
研究２０用冷拔双相钢丝在５００℃不同时间回火时延伸率的变化。
2.
The optimmum production technolgy of the dual phase steel wire has been studied with orthogonality and regressive orthogonality test method, and the regression equations has been established.
本文利用正交与回归正交试验法研究了双相钢丝的最佳生产工艺，并且建立了回归方程。
3.
15C dual phase steel wire.
15C双相钢丝的拉伸强度-冷拔减面率关系曲线。
5) dual-phase stainless steel wire
双相不锈钢丝
1.
To research mechanical property, drawing property and corrosion resistance of SUS329J dual-phase stainless steel wire after solution treatment at different temperatures.
研究SUS32 9J双相不锈钢丝在不同固溶处理温度下的力学性能、拉拔性能、耐蚀性能 ,与SUS30 4不锈钢丝进行比较结果表明 ,SUS32 9J双相不锈钢丝的屈服强度是SUS30 4奥氏体不锈钢丝的 2～ 3倍 ,其面缩率、延伸率、拉拔变形能力均较SUS30 4奥氏体不锈钢丝低 ,但具有较SUS30 4奥氏体不锈钢丝更高的耐蚀性能。
6) 20 steel
20钢
1.
Effect of tensile strain rate on spall fracture in 20 steel;
拉伸应变率对20钢层裂特性的影响
2.
TiC penetration and depositing on 20 steel surface by double-glow plasma alloying;
20钢表面双辉渗镀TiC陶瓷
3.
Flashing butt welding between ferrite spheroidal graphite cast iron and 20 steel;
铁素体球墨铸铁与20钢的闪光对焊