1) LC9 superduralumin alloy
LC9超硬铝
1.
The experiment on linear friction welding of LC9 superduralumin alloy was carried out by self-made linear friction welder,and the tensile test and analysis on metallographic structure of the welded specimens was conducted.
用自制的线性摩擦焊机进行了LC9超硬铝线性摩擦焊工艺试验,并对焊后试件进行了拉伸试验及金相组织分析。
2) LC9 aluminium alloy
LC9铝合金
1.
The superplastic deformation behavior of commercial LC9 aluminium alloy via annealing at 400℃ was studied by tensile testing.
通过拉伸实验研究了供应态LC9铝合金经退火处理后的超塑性变形特性。
3) super-hard aluminum
超硬铝
1.
A thick ceramic film was deposited on LC4 super-hard aluminum by microarc oxidation technique(MAO).
用微弧氧化方法在LC4超硬铝合金表面获得较厚的氧化膜,测定了氧化膜的生长曲线及电流密度变化,并用电化学方法测定不同厚度膜的极化曲线,采用零电阻技术测量3。
4) L C9CS surperhard aluminum alloy
LC9CS超硬铝
5) semi-solid LC9 aluminum alloy
半固态LC9铝合金
1.
The effects of deformation,heating temperature and holding time on microstructure of LC9 alloy in producing semi-solid billet by strain induced melt activated(SIMA) process were studied and structure evolution of semi-solid LC9 aluminum alloy was observed.
对冷变形金属进行等温加热转变制备半固态LC9铝合金坯料,并对其工艺过程及组织演变进行了研究,讨论了变形量、加热温度和保温时间等工艺参数对LC9铝合金组织的影响。
补充资料：普通硬铝
分子式：
CAS号：
性质：在Al-Cu系合金基础上发展起来的具有较高力学性能的可压力加工铝合金。又称硬铝合金和杜拉铝。属于可热处理强化类。包括Al-Cu-Mg系和Al-Cu-Mn系的合金。其中含有Cu2%～7%，Mg<3%，Mn<1%。这类合金一般为σb为400～460MPa，而且有较好的高温性能和满意的塑性。通常把Al-Cu-Mg系硬铝称为普通硬铝，其中铜和镁的总含量越高，镁铜含量的比值越大，热处理强化效果增加，合金的强度和硬度随之提高。而常把Al-Cu-Mn系硬铝合金称为耐热硬铝，在淬火人工时效状态下使用。硬铝合金在航空工业中应用广泛，但耐腐蚀性较低，其制品需要进行防腐处理，如包铝、阳极氧化和涂漆等。
CAS号：
性质：在Al-Cu系合金基础上发展起来的具有较高力学性能的可压力加工铝合金。又称硬铝合金和杜拉铝。属于可热处理强化类。包括Al-Cu-Mg系和Al-Cu-Mn系的合金。其中含有Cu2%～7%，Mg<3%，Mn<1%。这类合金一般为σb为400～460MPa，而且有较好的高温性能和满意的塑性。通常把Al-Cu-Mg系硬铝称为普通硬铝，其中铜和镁的总含量越高，镁铜含量的比值越大，热处理强化效果增加，合金的强度和硬度随之提高。而常把Al-Cu-Mn系硬铝合金称为耐热硬铝，在淬火人工时效状态下使用。硬铝合金在航空工业中应用广泛，但耐腐蚀性较低，其制品需要进行防腐处理，如包铝、阳极氧化和涂漆等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。