您的位置:首页 -> 词典 -> 硬铝
1)  duralumin [英][djuə'ræljumin]  [美][dju'ræljumɪn]
硬铝
1.
On the basis of the analysis of cold extrusion process for the duralumin drive wheel,the scheme,the drawing and the blank dimension of cold extrusion were worked out.
硬铝主动轮的冷挤压工艺进行分析,确定了冷挤压零件图和冷挤压方案及毛坯尺寸,对零件冷挤压的变形程度进行了校核,计算了挤压吨位,拟定了挤压前的毛坯处理规范,并对模具结构进行了介绍。
2.
The process for brush plating mending of deeply scratched surface of LY12 duralumin alloy was introduced.
研究了电刷镀技术在LY12硬铝合金零部件表面深度损伤修复中的应用,提出了电刷镀修复LY12硬铝合金零部件的工艺流程及条件。
2)  duralumin [英][djuə'ræljumin]  [美][dju'ræljumɪn]
硬铝杜拉铝
3)  duration [英][dju'reɪʃn]  [美][du'reʃən]
硬铝,杜拉铝
4)  LC9 superduralumin alloy
LC9超硬铝
1.
The experiment on linear friction welding of LC9 superduralumin alloy was carried out by self-made linear friction welder,and the tensile test and analysis on metallographic structure of the welded specimens was conducted.
用自制的线性摩擦焊机进行了LC9超硬铝线性摩擦焊工艺试验,并对焊后试件进行了拉伸试验及金相组织分析。
5)  super-hard aluminum
超硬铝
1.
A thick ceramic film was deposited on LC4 super-hard aluminum by microarc oxidation technique(MAO).
用微弧氧化方法在LC4超硬铝合金表面获得较厚的氧化膜,测定了氧化膜的生长曲线及电流密度变化,并用电化学方法测定不同厚度膜的极化曲线,采用零电阻技术测量3。
6)  aluminium-bearing hard zinc
铝硬锌
补充资料:标准硬铝合金


标准硬铝合金
middle strength duralumin alloy

  b iaozhuD yinglu he!in标准硬铝合金(middlestrength duraluminalloy)铝一铜一镁系中具有中等强度的合金,中国牌号为2All(L Yll),美国牌号为2017。它是一种最早的硬铝型合金,在2024(美国牌号)合金出现之前,就以各种形式的产品在结构中应用。现在,ZAn合金主要加工成棒材,供制造锻件和模锻件。 主要合金成分(%)为Al一Cu(3.8~4.8卜Mg(0 .4一0 .8)一Mn(o·4~0.5)。主要强化相为O(CuA12)相,当杂质硅含量低时,还有少量S(Al刃uMg)相(见铝合金的相)。 标准硬铝合金在工业生产中其熔炼温度为720一760℃,铸造温度为700一725℃,均匀化温度为495℃。热态塑性变形性能好,可加工成板、管、棒、型材和锻件,热轧温度390~4400C,挤压温度400一460℃,锻造温度350一470℃。热处理强化效果大,淬火温度50吐全℃,一般采用自然时效,96h以上可获得合格的性能。 ZAn合金的典型室温力学性能为:退火状态,。、为180MPa,丙.2为7oMPa,a为20%;在淬火+自然时效状态,。b为425MPa,ao.2为275MPa,a为20%。在大气中耐腐蚀性能中等,不耐海水腐蚀,包铝、阳极化处理和涂漆可提高耐腐蚀性能。不能钎焊和气焊,可氢弧焊,但焊接性能较低,点焊焊接性能较好。退火状态下切削性能低,充分自然时效的材料切削性能良好。 该合金用于制造中等强度的结构件,如在航空工业中制造飞机骨架、固定用接头和螺旋桨叶等;在建筑、造船和车辆工业中制造各种结构件和配件。 (张君尧)
  
说明:补充资料仅用于学习参考,请勿用于其它任何用途。