1) corundum-mullite materials
刚玉-莫来石
1.
The effect of NaF on the synthesis of corundum-mullite materials from high aluminum fly ash;
NaF对高铝粉煤灰合成刚玉-莫来石材料的影响
2.
In this paper,the influence of temperature and Li2O on the properties,crystal structure,and morphology of corundum-mullite materials prepared from fly ash and bauxite was studied.
研究了Li2O、烧结温度对高铝粉煤灰和铝矾土合成刚玉-莫来石材料的性能、物相组成和显微结构的影响。
2) corundum-mullite
刚玉莫来石
1.
Effects of micro-powder and firing temperature on microstructure and properties of corundum-mullite materials;
微粉及烧成温度对刚玉莫来石材料结构的影响
3) mullite-corundum
莫来石-刚玉
1.
Lightweight mullite-corundum materials were prepared by a gel-casting method,using bauxite,silica fume and polystyrene ball as starting materials.
以高铝矾土、硅灰、聚苯乙烯球作原料,用凝胶注模工艺制备高强轻质莫来石-刚玉材料,确定最佳pH值和分散剂用量,并研究了烧成后样品的强度、气孔率、热导率、物相组成和微观结构。
4) corundum/mollite
刚玉-莫来石相
1.
The experimental results show that the microstructure of the new ceramic tile can be improved by mending the present formula,decreasing the percentage of voids and increasing the corundum/mollite,and that the bulk density,compr.
实验研究结果表明,通过优化现有陶瓷墙地砖的工艺配方,改善陶瓷墙地砖微观结构,有利于降低陶瓷墙地砖的气孔率,提高陶瓷墙地砖的致密度和刚玉-莫来石相含量,可获得导热系数为2。
6) zirconia corundum-mullite
锆刚玉-莫来石
补充资料：刚玉-莫来石陶瓷
分子式：
CAS号：
性质：刚玉(α-Al2O3)和莫来石(3Al2O3,2SiO2)为主晶相的陶瓷。具有机械强度高、绝缘性能好的特点。相对介电常数6～7。介质损耗角正切值(14～18)×10-4［MHz,(20±5)℃) ］。体积电阻率1013～1014Ω·cm。击穿强度30～35kV/mm。线膨胀系数约4×10－6/℃ (20～100℃)。主要原料为氧化铝、高岭土和少量添加剂。用一般陶瓷工艺在1350℃左右烧成。可用于制造各种类型的高压绝缘子、套管、高压开关和其他装置零件。
CAS号：
性质：刚玉(α-Al2O3)和莫来石(3Al2O3,2SiO2)为主晶相的陶瓷。具有机械强度高、绝缘性能好的特点。相对介电常数6～7。介质损耗角正切值(14～18)×10-4［MHz,(20±5)℃) ］。体积电阻率1013～1014Ω·cm。击穿强度30～35kV/mm。线膨胀系数约4×10－6/℃ (20～100℃)。主要原料为氧化铝、高岭土和少量添加剂。用一般陶瓷工艺在1350℃左右烧成。可用于制造各种类型的高压绝缘子、套管、高压开关和其他装置零件。