1) epoxy modified polysiloxane
环氧改性硅油
1.
Preparation,characterization and application of epoxy modified polysiloxanes;
环氧改性硅油的制备与表征及应用进展
2) polyether modified water soluble silicone fluid
环氧改性水溶性硅油
3) epoxy modified silicone
环氧改性有机硅
1.
Anticorrosive epoxy modified silicone urethane paint was prepared with self-made epoxy modified silicone resin,pigments, functional fillers and additives.
采用环氧601树脂和自制低相对分子质量有机硅树脂进行共缩合反应制得环氧树脂改性有机硅树脂,并以此改性树脂为基料,加入颜料、功能性填料、助剂等研制出耐高温自干型环氧改性有机硅聚氨酯防腐蚀涂料。
2.
By evaluating the overall performance,the optimized formulation of the coating was found to be as follows: epoxy modified silicone resin SMH-30 50%-60%,micaceous iron oxide gray 22%-30%,sericite 9%-14%,curing agent 4.
通过对涂层的综合性能测试,确定涂料的优化配方为(质量分数):环氧改性有机硅树脂SMH-30 50%~60%、云母氧化铁灰22%~30%、绢云母9%~14%、固化剂4。
4) silicon-modified epoxy
有机硅改性环氧
1.
A novel low molecular silicon-modified epoxy resin with good phase compatibility was prepared through reaction of silicon oil with active hydrogen,epoxy resin and alcohol.
制备了相容性较好的低分子有机硅改性环氧树脂,配制了两种不同温度环境下的双组分高渗透型有机硅改性环氧防腐胶,讨论了浆料中双组分配比、环境温度、催干剂、有机硅改性环氧树脂和有机硅含量等对浆料的固化、渗透性、强度和憎水性能及防腐性能的影响,提出了浆料的几个主要应用实践与方向。
5) epoxysilicone fluid
环氧硅油
6) modified silicone fluid
改性硅油
1.
The polyether modified branched chain silicone fluid,ethyleneoxy polyether modified silicone fluid,polyether-ended long chain alkyl silicone fluid,glycerol ether and polyether co-modified silicone fluid,the characteristics,structure and synthesis method of f digenetic silicone surfactant containing lycine were introduced.
介绍了聚醚改性支链硅油、乙烯氧基聚醚改性硅油、聚醚封端的长链烷基硅油、甘油醚与聚醚共改性硅油、含甜菜碱基的两性有机硅表面活性剂的性能、结构及合成方
2.
The characteristics,structure,synthesis methods and application of anion silicone surfactant,polyether containing phenolic group/arylno modified silicone fluid,reactivity polyorganosilicone/polylactone copolymer,and containing glucosyl silicone surfactant were introduced.
介绍了阴离子型有机硅表面活性剂、含酚基或芳氨基的聚醚改性硅油、反应性聚有机硅氧烷/聚内酯共聚物、含糖基的有机硅表面活性剂的特点、结构、合成方法及应用。
补充资料：有机硅改性环氧树脂
分子式：
CAS号：
性质：电绝缘性能优异，介电强度103kV/mm(常态)，57kV/mm(受潮)，65kV/mm(200℃)；体积电阻率2×1016Ω·cm(常态)。涂在铜片上的漆膜200℃，168h老化不开裂，250℃，12h后热失重为4.15%，粘接强度2.1MPa。可由含烷氧基或羟基的低分子量聚硅氧烷与双酚基丙烷环氧树脂进行缩合反应来制取。用作H级电机、电器、变压器线圈浸渍漆，电缆接头和电子元件表面保护涂料。还可与玻璃布复合制成层压材料。
CAS号：
性质：电绝缘性能优异，介电强度103kV/mm(常态)，57kV/mm(受潮)，65kV/mm(200℃)；体积电阻率2×1016Ω·cm(常态)。涂在铜片上的漆膜200℃，168h老化不开裂，250℃，12h后热失重为4.15%，粘接强度2.1MPa。可由含烷氧基或羟基的低分子量聚硅氧烷与双酚基丙烷环氧树脂进行缩合反应来制取。用作H级电机、电器、变压器线圈浸渍漆，电缆接头和电子元件表面保护涂料。还可与玻璃布复合制成层压材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。