1) epoxy-modified polysiloxane
环氧基改性聚有机硅氧烷
2) Organically modified polysiloxane
有机改性聚硅氧烷
3) epoxy modified silicone
环氧改性有机硅
1.
Anticorrosive epoxy modified silicone urethane paint was prepared with self-made epoxy modified silicone resin,pigments, functional fillers and additives.
采用环氧601树脂和自制低相对分子质量有机硅树脂进行共缩合反应制得环氧树脂改性有机硅树脂,并以此改性树脂为基料,加入颜料、功能性填料、助剂等研制出耐高温自干型环氧改性有机硅聚氨酯防腐蚀涂料。
2.
By evaluating the overall performance,the optimized formulation of the coating was found to be as follows: epoxy modified silicone resin SMH-30 50%-60%,micaceous iron oxide gray 22%-30%,sericite 9%-14%,curing agent 4.
通过对涂层的综合性能测试,确定涂料的优化配方为(质量分数):环氧改性有机硅树脂SMH-30 50%~60%、云母氧化铁灰22%~30%、绢云母9%~14%、固化剂4。
4) silicon-modified epoxy
有机硅改性环氧
1.
A novel low molecular silicon-modified epoxy resin with good phase compatibility was prepared through reaction of silicon oil with active hydrogen,epoxy resin and alcohol.
制备了相容性较好的低分子有机硅改性环氧树脂,配制了两种不同温度环境下的双组分高渗透型有机硅改性环氧防腐胶,讨论了浆料中双组分配比、环境温度、催干剂、有机硅改性环氧树脂和有机硅含量等对浆料的固化、渗透性、强度和憎水性能及防腐性能的影响,提出了浆料的几个主要应用实践与方向。
6) amino-modified polyorganosiloxane
氨基改性聚硅氧烷
1.
s:The amino-modified polyorganosiloxane and its microemulsi on were prepared by means of bulk and emulsion polymerization.
分别采用本体聚合法和乳液聚合法制备了氨基改性聚硅氧烷及其微乳液 ,讨论了影响聚合反应及其微乳液的各种因素。
补充资料：氧杂环戊烷
分子量72．11。无色透明液体。有类似乙醚气味。相对密度(20 ℃／4℃)0.8892，凝固点-108．5℃，沸点66℃．闪点(闭口)17．2℃，燃点321．1℃，折射率1. 4073，粘度(20 ℃)0.55mPa·s，表面张力26．4×10-3N／m，溶解度参数δ=9．2。能与水、醇、醚、酮、酯、烃类多种有机溶剂混溶。易燃，与氢氯化钠、氢氢化钾反应强烈。与酸接触能发生反应，不加稳定剂暴露在空气中能形成有爆炸性的过氧化物。蒸气能与空气形成爆炸性混合物，爆炸极限2．3％-11．85％(vol)。有毒，具有麻醉作用，空气中最高容许浓度590mg／m3(或0.02%)。
用作溶剂，可配制聚氯乙烯胶粘剂和氟塑料处理剂。贮存于阴凉、通风、干燥的库房内，远离火种、热源，防止日光直射。
用作溶剂，可配制聚氯乙烯胶粘剂和氟塑料处理剂。贮存于阴凉、通风、干燥的库房内，远离火种、热源，防止日光直射。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条