1) friction material
摩阻材料
1.
Research on friction materials and their static frictional properties;
摩阻材料的研制及其静摩擦因数变化规律
2.
A new type of friction material was prepared with carbon fiber and steel fiber as reinforcements and FB polymerized phenolic as matrix resin by mould pressing technology.
采用碳纤维和钢纤维为增强材料、硼酚醛树脂为基体,通过模压成型制得新型混杂纤维增强树脂基摩阻材料。
3.
To obtain resin matrix of friction material with high-quality,tung oil was used to modify phenolic resin.
利用桐油改性酚醛树脂(PF),制备高性能摩阻材料用树脂基体。
2) frictional materials
摩阻材料
1.
Maximal hardness of frictional materials is 88.
纤维增强摩阻材料的抗冲击韧性和硬度对摩擦学性能有一定影响,但并不惟一决定摩擦系数和磨损率的大小。
2.
Through testing by Japanese JXA-840 SEM,it is found that fiber frac ture,fiber pullout,fiber bridge,interface debonding,crack branching and veer mak e a great contribution to impact toughness increase of frictional materials.
利用日本JXA-840型扫描电子显微镜(SEM)对研制的新型摩擦制动材料冲击断口进行测试,结果表明纤维的断裂、纤维的拔出、纤维的桥接、界面脱粘及裂纹分叉、转向对提高摩阻材料的冲击韧性有极大的贡献,纤维对主裂纹的发展有阻碍作用,延缓了主裂纹的增长速度,在其他条件不变的情况下,纤维拔出的长度增加,吸收能量增大,材料的冲击强度也提高。
3.
This article studies semimetal frictional materials on the basic ingredients.
综述了半金属摩阻材料基本组成、性能特点、生产工艺及摩擦磨损机理，着重讨论了各组元对半金属摩阻材料在物理化学性能、摩擦磨损性能等方面的影响，介绍了国内外在此研究领域的现状，并结合作者目前从事的研究对本方向可继续进行的研究工作提出了建议。
3) friction materials
摩阻材料
1.
The development and prospect of friction materials;
摩阻材料的发展历程与展望
2.
The effects of matrix modification of resin matrix friction materials on friction and wear of friction couple,which was composed of resin matrix friction materials and aluminum matrix composites were studied under dry sliding.
研究了树脂基摩阻材料的基体共混改性对树脂基摩阻材料/喷射沉积铝基复合材料摩擦副在干摩擦状态下摩擦磨损性能的影响,着重探讨了腰果壳油改性酚醛树脂与丁腈橡胶(NBR)的比例对摩擦副的影响,在此基础上制备出了用于1∶1台架制动试验的树脂基闸片。
3.
The paper studies effects of T6 heat treatment on friction and wear of A359/SiCp composites fabricated by spray deposition, characteristic of the movable crucible, in dry sliding with polymer matrix friction materials.
研究了T6热处理对坩埚移动式喷射沉积A359/SiCp复合材料与树脂基摩阻材料在干摩擦状态下摩擦磨损性能的影响,结果表明:经过T6热处理,可以提高材料的硬度和耐磨性能,改善摩擦系数的稳定性,当采用530℃固溶3h水淬,随后175℃时效7h热处理工艺,A359/SiCp复合材料的磨损率为未热处理喷射沉积态时的1/10。
4) frictional material
摩阻材料
1.
B 4C was added into the NBR modified phenolic resins which was further used to prepare frictional materials.
研究了在丁腈改性酚醛树脂中掺杂B4C制备的摩阻材料的性能。
2.
A new type of non asbestos frictional material is developed, which is made of phenolic resin, glass fiber, alumina,silicon oxide, barium sulfate, copper powder and graphite.
以酚醛树脂、玻璃纤维、氧化铝、氧化硅、硫酸钡、铜粉及石墨等为原料按一定的配比制得了一种新型的摩阻材料并测试了其摩擦磨损特性。
3.
In this paper,the decomposition activating energy (E) of different matrixes was calculat-ed by TGA,the thermosetting temperature curve of the matrixes frictional material was de-termined by DSC,the S.
本文采用DSC、TGA和DDV等热分析手段对聚合物基摩阻材料进行了分析研究。
5) rare earth frictional material
稀土摩阻材料
1.
In the process of preparing a new type rare earth frictional material,the influence of resin agglomerate,thiokol modified phenol-formaldehyde resin,contents on property of friction material was studied.
在制备的新型稀土摩阻材料中 ,研究了丁腈改性酚醛树脂粘结剂含量变化对材料性能的影响。
6) composite frictional material
复合摩阻材料
1.
First,combined with local resources,the no asbestos CFRP composite frictional material has been investigated,which function excels abroad.
首先结合地区资源优势,开发成功性能优于摩阻材料的碳纤维无石棉复合摩阻材料,另外开发了制动块背板的精冲工艺。