1) 13Cr-L-80 Steel
13Cr-L-80钢
2) alloy steel 13Cr-L-80
合金钢13Cr-L-80
3) 13Cr steel
13Cr钢
1.
The carbon dioxide corrosion experiments at high temperature and high pressure of ordinary 13Cr steel were done at the environment of DA QING oil field.
针对普通13Cr钢的CO2抗腐蚀性能,模拟大庆油田井下的腐蚀环境,通过高温高压釜进行了13Cr钢的腐蚀试验。
2.
The results show that under the three temperatures,the corrosion types of 13Cr steel in the liquid phase are all general corrosion and N80 steel are local corrosion.
结果表明,在所试验的三个温度下,13Cr钢液相腐蚀类型主要为均匀腐蚀,N80钢主要是局部腐蚀。
3.
Three 13Cr steels were tested in simulated CO_2 environment with autoclave to evaluate and compare their corro- sion behavior.
为了对比评价3种13Cr钢耐CO_2腐蚀性能,在模拟CO_2腐蚀环境中,采用高温高压釜对3种钢的CO_2腐蚀行为进行了试验研究。
4) 13Cr stainless steel
13Cr不锈钢
1.
The effects of EPS on the pitting sensitivity of 13Cr stainless steel were studied by electrochemical technology.
从渤海油田分离嗜热硫酸盐还原菌(SRB),用电化学测试技术研究其胞外高聚物(EPS)活性对13Cr不锈钢点蚀敏感性的影响。
5) Enhancement 13Cr steel
增强型13Cr钢
6) 80 steel
80钢
1.
It is pointed out by the brittle fracture appearance observation of 80 steel wire rod and microstructure analysis that the plastic distortion of basal metal and dislocation adding at surface damage position are the main cause of wire drawing breaking.
通过对80钢盘条脆断断口形貌观察和金相组织分析,认为盘条表面损伤部位的金属基体产生塑性变形和位错增加是拉拔断丝的主要原因,在高碳钢生产及吊装运输中应采取措施避免盘条擦伤,以提高产品质量。
补充资料：Direx 80W
分子式：C9H10Cl2N2O
分子量：233.09
CAS号：330-54-1
性质：熔点158-159°C。水溶性Slightly soluble. 0.0042 g/100 mL。
分子量：233.09
CAS号：330-54-1
性质：熔点158-159°C。水溶性Slightly soluble. 0.0042 g/100 mL。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条