It is pointed out by the brittle fracture appearance observation of 80 steel wire rod and microstructure analysis that the plastic distortion of basal metal and dislocation adding at surface damage position are the main cause of wire drawing breaking.
通过对80钢盘条脆断断口形貌观察和金相组织分析,认为盘条表面损伤部位的金属基体产生塑性变形和位错增加是拉拔断丝的主要原因,在高碳钢生产及吊装运输中应采取措施避免盘条擦伤,以提高产品质量。
4) 13Cr-L-80 Steel
13Cr-L-80钢
5) 80 steel wire rod
80钢盘条
1.
To introduce production process flow and mechanical properties of high strength 80 steel wire rod.
介绍高强度80钢盘条的生产工艺流程和力学性能指标,通过金相组织分析,指出钢的组织中出现网状渗碳体是拉拔断裂的主要原因,采用人工时效并改进拉拔工艺,使各道次的压缩率均匀合理,在一定程度上可以弥补组织不当带来的缺陷,有利于盘条的拉拔。
2.
By means of microstructure test,chemical composition analysis,fracture test,inclusion spectrum analysis of 80 steel wire rod with lower strength and bigger plasticity variety,the results show that the cause of lower strength is lower content of sorbite and the reasons for bigger plasticity variety are meshy carbides and big grain brittle inclusions inside the wire rod.
通过对强度偏低、塑性变化较大的80钢盘条的金相检验、化学成分分析、断口检验、夹杂物能谱分析,认为其强度偏低的原因是索氏体含量偏低,塑性变化较大的原因是盘条内部存在网状碳化物和大颗粒脆性夹杂物。
6) T8A(80) steel
T8A(80)钢
补充资料：AAtrex 80W
分子式：C8H14ClN5
分子量：215.68
CAS号：1912-24-9
性质：密度1.187。熔点175°C。沸点200°C。水溶性Slightly soluble. 0.007 g/100 mL。
分子量：215.68
CAS号：1912-24-9
性质：密度1.187。熔点175°C。沸点200°C。水溶性Slightly soluble. 0.007 g/100 mL。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条