1) super 13Cr stainless steel
超级13Cr不锈钢
2) 13Cr stainless steel
13Cr不锈钢
1.
The effects of EPS on the pitting sensitivity of 13Cr stainless steel were studied by electrochemical technology.
从渤海油田分离嗜热硫酸盐还原菌(SRB),用电化学测试技术研究其胞外高聚物(EPS)活性对13Cr不锈钢点蚀敏感性的影响。
3) Super Stainless Steel
超级不锈钢
4) super duplex stainless steel
超级双相不锈钢
1.
The tensile properties at 900-1300℃,as well as the deformed microstructure of the as-forged 00Cr25Ni7Mo4N super duplex stainless steel(SDSS)have been studied by thermo-mechanical simulator.
用Gleeble-3800热变形模拟试验机研究了锻态00Cr25Ni7Mo4N超级双相不锈钢在900~1300℃时的高温拉伸塑性和高温变形组织特征。
2.
The effect of the heat treatment on the dual phase scale and corrosion property of the super duplex stainless steel 00Cr25Ni7MoN have been introduced in this article.
本文介绍了热处理工艺对超级双相不锈钢00Cr25N i7Mo4N中两相的比例有影响,进而对该钢的耐腐蚀性能也造成影响的试验分析情况。
3.
The influence of rare earths on solidification structure of 00Cr25Ni7Mo4N super duplex stainless steel was studied.
研究了Ce对00Cr25Ni7Mo4N超级双相不锈钢凝固组织的影响,结果表明,随着钢中Ce含量的增加,其凝固组织中等轴晶线性比相应明显增加,Ce含量为0%,0。
5) super austenitic stainless steel
超级奥氏体不锈钢
1.
The concept of super austenitic stainless steel appeared with super ferrite stainless steel and super double phases stainless steel together.
超级奥氏体不锈钢的概念是与超级铁素体不锈钢及超级双相不锈钢一起出现的。
2.
The liquids of N08904 super austenitic stainless steel was computed and tested by means of theoretical calculation and thermal analysis,reasonable overheat was put forward and leaking problem of molten steel during continuous casting was solved and continuous casting production had come into effect.
采用理论计算与热分析相结合的方式对N08904超级奥氏体不锈钢的液相线温度进行了计算测试,提出了合理的过热度参数,解决了连铸易漏钢问题,实现了连铸生产。
3.
The results showed that Cr20Ni18Mo6MnVSi super austenitic stainless steel in the chloride solution had excellent corrosion resistance properties after solution treatment at 1100℃ for 2h and followed by the aging treatment at 520℃ for 4h.
1型超级奥氏体不锈钢经1100℃固溶2h+520℃时效4h处理后,在高浓度氯离子溶液中的耐腐蚀性能优异。
6) Super Duplex Stainless Steel 00Cr25Ni7Mo4N
超级双相不锈钢00Cr25Ni7Mo4N
1.
Influence of Solution Temperature on Structure and Properties of Super Duplex Stainless Steel 00Cr25Ni7Mo4N;
固溶温度对超级双相不锈钢00Cr25Ni7Mo4N组织和性能的影响
补充资料:Ti-13V-11Cr-3A1 alloy
分子式:
CAS号:
性质:β钛合金。成分为钒13%,铬11%,铝3%,余量钛。退火后室温机械性能:抗拉强度862MPa,屈服强度827MPa,延伸率10%,弹性模量10.34×104MPa,HRC硬度32~36。采用真空自耗电弧炉熔炼制取。制造紧固件和较大面积的模锻件。
CAS号:
性质:β钛合金。成分为钒13%,铬11%,铝3%,余量钛。退火后室温机械性能:抗拉强度862MPa,屈服强度827MPa,延伸率10%,弹性模量10.34×104MPa,HRC硬度32~36。采用真空自耗电弧炉熔炼制取。制造紧固件和较大面积的模锻件。