1) melting rate
熔速
1.
Effect of atmosphere and addition agent on the melting rate of low carbon mold powder in continuous casting;
气氛和添加剂对低碳连铸保护渣熔速的影响
2.
Change of both slag temperature and melting rate in three different refining processes are presented as follows.
对三种工艺下的渣温、熔速进行了讨论并得到如下结果:恒功率重熔——渣温、熔速随锭高线性增加;恒熔速重熔——渣温,熔速在过程中保持恒定;恒熔池深度重熔——渣温、熔速随过程降低。
2) Melting speed
熔速
1.
Two kinds of methods of controlling melting speed for ESR furnace is indicated,Then computer control system and its tast for ESR furnace is researched.
阐述了我国电渣炉计算机控制的过去和现状,提出电渣炉两种熔速控制方案,据此阐明了计算机控制系统配置和它们的任务。
3) fast dissolving
速熔
1.
On the basis of the domestic and foreigh aluminum alloy additive,this article research a new aluminum alloy additive,which have the advantage of fast dissolving,high efficiency and wide appli.
本文在总结国内外铝合金添加剂的基础上,提出了一种新型高效速熔铝合金添加剂的研制方法。
4) flash smelting
闪速熔炼
1.
Research on the Matte Temperature Model of Copper Flash Smelting Process Based on ANFIS;
基于自适应模糊神经网络的铜闪速熔炼冰铜温度模型研究
2.
Progress and research of flash smelting in China ——Cold air technology and "non-contact metallurgy;
闪速熔炼在中国的进展与研究——冷风技术及“非接触冶金”
5) Zone melting rate
区熔速率
6) melting speed
熔化速度
1.
Study on melting speed of continuous casting mold powder;
含碳材料对连铸保护渣熔化速度影响的研究
2.
The burning loss of carbon is a key factor that controls the melting speed of mold powder.
利用碳烧损量是控制保护渣熔化速度的关键因素这一原理,用失重法检测了不同温度下保护渣的烧损量并尝试用于比较其熔化速度。
3.
The melting speed of low carbon CC mold flux composed of different carbon materials(graphite and active carbon) and different carbon mass fraction((2.
2%)的低碳连铸保护渣在空气中和在氩气中的熔化速度,结果是在有惰性气体保护下的熔化速度远小于一般在空气中的熔化速度。
补充资料：熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
production of niobium powder by molten salt electrolysis
rongyand+onjlefa ShengChan n.fen熔盐电解法生产妮粉(produetion。fn;obi-um powder by molten salt eleetrolysls)见熔盐电解法生产担粉。