1) conductive composite
导电复合材料
1.
Preparation and characterization of CdS/poly-aniline conductive composite materials;
CdS/聚苯胺导电复合材料的制备与表征
2.
Influences of carbon black content,crosslinker,foamer on conductive properties of PVC/CB foaming conductive composites were investigated.
以特导炭黑(CB)为导电填料,聚氯乙烯(PVC)和三元乙丙橡胶(EPDM)为主基体制备PVC泡沫导电复合材料,研究该复合材料的泡孔结构和阻温特性,分析炭黑含量、交联剂和发泡剂对复合材料电性能的影响。
3.
Electrical conductive composites were fabricated by hotpressing at 140 ℃ using epoxy resin filled with ultra-fine Fe-Cr fibers.
通过大量拉拔变形制备了Cu-F e-C r原位复合材料并萃取出其中的F e-C r纤维,以超细F e-C r纤维为导电填料,填充环氧树脂,140℃热压制得导电复合材料。
2) conductive composites
导电复合材料
1.
Preparation and conductive behavior of expanded graphite/poly-(ethylene terephthalate) conductive composites;
膨胀石墨/聚酯导电复合材料的制备与导电行为
2.
Progress of polymer matrix conductive composites;
聚合物基导电复合材料研究进展
3.
Development of carbon black/polyurethane foaming conductive composites;
炭黑/聚氨酯泡沫导电复合材料的开发
3) conducting composite
导电复合材料
1.
Research on PTC effect in carbon/polymer conducting composites;
炭黑高聚物导电复合材料PTC效应的研究
2.
Phenomenal analysis of percolation and PTC behavior in conducting composite with short carbon fiber;
短切碳纤维导电复合材料渗流和PTC行为的唯象分析
3.
The preparation method of PU-based polyaniline conducting composite was reviewed,including copolymerization/graft polymerization,in situ polymerization,solution/emulsion/mechanical blending,and chemical/electrochemical methods.
概述了聚氨酯与新型导电聚合物聚苯胺的复合材料的制备原理、工艺及性能等,包括聚氨酯内部渗透法、聚苯胺包裹法、共聚/接枝及化学氧化/电化学聚合等,对应用不同制备方法制作的聚氨酯/聚苯胺导电复合材料的性能做了比较,并对聚氨酯/聚苯胺导电复合材料的研究前沿和应用前景做了介绍。
4) conductive composite material
导电复合材料
1.
Performance of PVDF/Ti_3SiC_2 conductive composite materials;
PVDF/Ti_3SiC_2导电复合材料的性能
5) conducting composites
导电复合材料
1.
Various influential factors of PTC effect on carbon/polymer conducting composites are summarized in the paper.
本文综述了炭黑／高聚物导电复合材料ＰＩＣ效应的影响因素，探讨了ＰＴＣ效应稳定化的途径。
2.
The low temperature exothermic conducting composites panels were systematically researched in this paperbased on large quantities of experiment.
在大量实验的基础上对低温面发热导电复合材料作了较为系统的研究，应用短切碳纤维改善了炭黑填充导电复合材料的电性能和力学性能，结果表明：少量短切碳纤维能明显改善导电粉末填充复合材料的导电性能。
3.
In this paper, distribution of iron powder in polymer matrix conducting composites was changed from random distribution to unidirectional arrangement under magnetic field, and fibriform iron powder was arrayed in the direction of magnetic flux.
本论文介绍了在外加磁场的条件下，聚合物基导电复合材料中铁粉取向由随机分布变为单向分布，并形成了与磁力线方向一致的纤维状铁粉，使导电复合材料的力学性能和导电性能呈各向异性。
6) PTC conductive polymeric composite
PTC复合导电材料
补充资料：导电复合材料
导电复合材料
electrical conducting composite materials
导电复合材料eleetrieal。ondueting eompositematerials导电材料和高分子绝缘材料复合得到的具有导电功能的材料。复合形式分为:①把导电性物质分散到高分子绝缘基体材料中;②将连续导电膜复合到绝缘支承体上(板膜，框架等)。有时只称前者为导电复合材料，而称后者为导电膜。 用不同的高分子基体材料，以第一种复合方法已分别开发出导电橡胶、导电塑料和导电涂料3大类导电复合材料。赋予复合材料导电功能的分散相物质有各种炭黑、碳纤维及镀金属的碳纤维、各种金属粉末及纤维(如不锈钢纤维)、经金属处理的无机粉末及纤维(如镀金属的玻璃微球和玻璃纤维)等。 制备导电复合材料的制备方法有3类:①聚合物粒子与导电粒子混合压制成型;②聚合物熔体或浓溶液与导电粒子混合后，经冷却或除去溶剂成型;③生胶或高分子单体与导电粒子混合后硫化或聚合成型。同样的配方，工艺条件不同，可以制备出导电性能差异很大的复合材料。这是与导电体能否形成导电通道有关。 性能不同方法制备的导电复合材料表现出一些共同性质:①材料导电率随导电体加入量变化呈非线性关系。在导电体加入之初，材料导电率增加极少;达某一阑值后，导电率跃升10个数量级以上，即复合材料开始成为导电材料。一般认为这一闭值对应于复合材料中导电体形成导电通道的临界状态。②导电率与温度有明显的依赖关系。随温度上升，导电率下降。这与金属的导电率一温度依赖关系类似，但导电机理不同。③具有开关效应或正温度系数电阻效应，即复合材料导电率随温度呈非线性变化。在某一温区，随温度升高复合材料的导电率迅速下降，可达7一8个数量级，由良导体变为绝缘体。 导电复合材料与金属导体相比，具有优良的加工性能，容易加工成所需的各种复杂结构和形状的部件，并可大批量生产;耐腐蚀，密度低，可供选择的柔软性和导电性范围大;可供选择材料的导电率范围大(lO--3一10，0昆·em);价格比较便宜。 应用导电复合材料因其优良的性能获得广泛的应用。最重要的应用有以下几方面:①接点和键盘材料。如导电硅橡胶用作计算机、计算器、打印机、电子乐器等的键盘接点材料。按不同要求使用寿命可达100一1000万次以上。为了使仪器小型化、薄型化，正把导电橡胶接点改变为导电涂料丝网印刷厚膜接点。②电磁波屏蔽。用导电塑料做电子仪器外壳或框架，以及用导电涂料在塑料外壳或框架上形成导电膜，都是防止电磁波干扰的有效方法。③防静电导电橡胶板用于大规模集成电路制造厂、手术台等，以及用作防爆泵导电外壳，电子元件封装材料，炸药等危险品的包装材料。④作恒温加热元件和电路过电流保护元件。利用导电复合材料的PTC效应，制成各种恒温加热器，如保温垫，水管、输油管加热套，建筑物加热器，镜子去雾加热器等，作大面积恒温加热。⑤印刷线路板、厚膜混合集成电路、厚膜电阻等。传统的印刷线路板是刻蚀铜箱方法制成的，现已制成导电涂料丝网印刷的线路板。 (胡乡鉴、
说明：补充资料仅用于学习参考，请勿用于其它任何用途。