1) microalloying element
微合金元素
1.
The results showed that the softening is restricted by the carbonitrides of microalloying elements Nb,V and Ti in the HSLA steel and,after 6-pass reduction,the austenite grain size is down to 8 μm through grain refining,i.
研究表明,对铌钒钛高强钢,微合金元素铌、钒、钛的碳氮化物能有效抑制奥氏体的高温软化行为,经过6道次变形的奥氏体晶粒细化到8μm左右,其控轧工艺为未再结晶区的控制轧制。
2) Micro Alloying Element
微合金元素
1.
By high temperature reduction experiment on Gleeble-1500 hot stimulation testing machine for steels 30MnSi and 30MnSiV, the effect of micro alloying element vanadium on deforming resistance under different deformation conditions was analyzed.
通过对 30 Mn Si和 30 Mn Si V两种钢在 Gleeble- 15 0 0热模拟试验机上的高温压缩变形实验 ,分析了不同变形条件下微合金元素钒对变形抗力的影响。
3) microalloy element
微合金元素
1.
The effect of several microalloy elements on hot plasticity of low alloy C Mn steel is introduced,its cause analysed.
介绍了几种微合金元素对低合金 Ｃ－ Ｍｎ 钢热塑性的影响，分析了这些微合金元素影响热塑性的原因。
2.
For the Ti Ni microalloy steel, adopting theory calculation and age hardening experiment method respectively, dissolve and precipitation of the microalloy element in the both austenite and ferrite have been analyzed.
针对铌、钛微合金钢,分别采用理论计算和时效硬度实验的方法,分析了微合金元素在奥氏体和铁素体中的溶解与析出。
4) microalloyed element
微合金元素
1.
Steel strength is enhanced by appending strengthening microalloyed element .
采用合理的成分设计,将主要合金元素的质量分数控制在较低水平,使其具有良好的焊接性能和较低的生产成本;采用微合金元素强化工艺以提高钢的强度,使用大电炉冶炼加LF精炼以保证钢的纯净度。
2.
To obtain better weldability and lower cost,main alloy element content is controlled at a lower level; to enhance steel strength,microalloyed element is appended; to make the steel clean, electric arc furnace and ladle furnace are appiled.
采用合理的成分设计,将主要合金元素含量控制在较低的水平,使钢具有良好的焊接性能和较低的生产成本;采用微合金元素强化工艺,提高钢的强度,使用大电炉冶炼加LF精炼,以保证钢的纯净度。
5) microalloying elements
微合金元素
1.
The causes and the factors affecting the formation of the cracks in continuously cast strand are summarized through analyzing the solidification behaviors and high temperature mechanism of steel,stress and strain acting on continuously cast strand,chemical component,presence behavior of microalloying elements.
文章从钢的凝固行为、高温力学性能、作用在连铸坯上的各种应力、应变、化学成分以及微合金元素析出行为等角度出发 ,总结分析了各主要因素对连铸坯产生裂纹的影响 ,对铸坯裂纹的形成条件、机理进行了综述和总结 ,探讨性地提出了防止连铸坯产生裂纹的对策方
6) microalloy element Nb
微合金元素泥
补充资料：合金元素
分子式：
分子量：
CAS号：
性质：组成合金的化学元素。多数是金属元素，如铜、锡、铅、铝、锰、铬、钼、镍及稀有金属等。少数是非金属元素，如碳、硅、磷等。
分子量：
CAS号：
性质：组成合金的化学元素。多数是金属元素，如铜、锡、铅、铝、锰、铬、钼、镍及稀有金属等。少数是非金属元素，如碳、硅、磷等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。