1.
The results showed that the softening is restricted by the carbonitrides of microalloying elements Nb,V and Ti in the HSLA steel and,after 6-pass reduction,the austenite grain size is down to 8 μm through grain refining,i.
研究表明,对铌钒钛高强钢,微合金元素铌、钒、钛的碳氮化物能有效抑制奥氏体的高温软化行为,经过6道次变形的奥氏体晶粒细化到8μm左右,其控轧工艺为未再结晶区的控制轧制。
4) Micro Alloying Element
微合金元素
1.
By high temperature reduction experiment on Gleeble-1500 hot stimulation testing machine for steels 30MnSi and 30MnSiV, the effect of micro alloying element vanadium on deforming resistance under different deformation conditions was analyzed.
通过对 30 Mn Si和 30 Mn Si V两种钢在 Gleeble- 15 0 0热模拟试验机上的高温压缩变形实验 ,分析了不同变形条件下微合金元素钒对变形抗力的影响。
5) microalloyed element
微合金元素
1.
Steel strength is enhanced by appending strengthening microalloyed element .
采用合理的成分设计,将主要合金元素的质量分数控制在较低水平,使其具有良好的焊接性能和较低的生产成本;采用微合金元素强化工艺以提高钢的强度,使用大电炉冶炼加LF精炼以保证钢的纯净度。
2.
To obtain better weldability and lower cost,main alloy element content is controlled at a lower level; to enhance steel strength,microalloyed element is appended; to make the steel clean, electric arc furnace and ladle furnace are appiled.
采用合理的成分设计,将主要合金元素含量控制在较低的水平,使钢具有良好的焊接性能和较低的生产成本;采用微合金元素强化工艺,提高钢的强度,使用大电炉冶炼加LF精炼,以保证钢的纯净度。
6) microalloy element
微合金元素
1.
The effect of several microalloy elements on hot plasticity of low alloy C Mn steel is introduced,its cause analysed.
介绍了几种微合金元素对低合金 Ｃ－ Ｍｎ 钢热塑性的影响，分析了这些微合金元素影响热塑性的原因。
2.
For the Ti Ni microalloy steel, adopting theory calculation and age hardening experiment method respectively, dissolve and precipitation of the microalloy element in the both austenite and ferrite have been analyzed.
针对铌、钛微合金钢,分别采用理论计算和时效硬度实验的方法,分析了微合金元素在奥氏体和铁素体中的溶解与析出。