1) FEP/PPS blending coatings
FEP/PPS共混涂层
2) PPS/FEP composite anti-corrosive coatings
PPS/FEP复合防腐涂层
1.
The bonding strength of PPS/FEP composite anti-corrosive coatings using various surface pretreatments such as grinding with emery paper,acid etching,phosphating and blasting was determined by the pull-off test.
采用拉开法测定了砂纸打磨、酸洗、磷化以及喷砂等多种表面处理条件下PPS/FEP复合防腐涂层的结合强度,用扫描电镜(SEM)和表面粗糙度测试仪分析了试样经各种表面处理后的表面形貌及粗糙度。
3) FEP coating
FEP涂层
1.
FEP coatings were prepared using flame spraying.
利用火焰喷涂在不同预热温度制备了FEP涂层,评价了环境温度对涂层摩擦学性能的影响,并对涂层进行了XRD、SEM等分析。
4) PPS coating
PPS涂层
1.
Polyphenylenesulphide(PPS) suspension dope was prepared using the method of mechanical mixing, and the PPS coating was prepared in metal surface through the process of high-temperature plastication.
对涂敷PPS涂层的Q235-A钢板试件在应力控制下进行了对称循环载荷疲劳试验,研究了材料的循环硬化软化特性。
5) blending coating
共混涂层
6) PPS/PES blends
PPS/PES共混物
1.
The compatibility, multiple transition and relaxation behaviour of PPS/PES blends and their composites reinforced by carbon fiber (CFPPS/PES) have been studied by internal friction analysis method.
本工作利用内耗测量方法研究了PPS/PES共混物及其碳纤维复合材料的相容性以及多重转变和松弛行为,结果表明:(1)PPS与PES存在分子运动水平上的相互作用,共混组份比是决定其相互作用程度的重要因素;(2)PPS/PES共混物及其碳纤维复合材料中的PES相的β转变与松弛的时间存在较宽的连续分布,其分布宽度随共混组份比变化而变化,当PES相对含量为80％时,松弛时间分布宽度出现最大值;(3)PPS/PES共混物及其碳纤维复合材料处于热力学亚稳态,热处理增大了PPS与PES的相分离程度,减弱了它们之间的相互作用;(4)低温区热历史对PPS玻璃化转变有较大影响,内耗峰高及峰温随起始测量温度的升高而下降。
补充资料：Pps冲锋枪
1930年代末，苏联一位著名的轻武器设计师乔治·s.斯帕金开始从事冲锋枪研究。他设计的第一支冲锋枪于1940～1941年初完成全面试验，1941年正式装备苏军，定型号为ppsh-41式冲锋枪。当时正处在苏联卫国战争最艰苦的时候，纳粹军队大兵压境，前线战事进行得非常不顺利，苏军节节败退，前方武器损失惨重，急需大量性能优良的轻武器补充部队。该冲锋枪研制成功后，于1942年开始批量生产，是苏军在第二次世界大战期间使用量最大的冲锋枪。
pps-42式冲锋枪是在第二次世界大战的硝烟中研制成功的，首批试生产就是在列宁格勒被德军重兵包围和全面封锁的艰苦条件下进行的，试生产的产品完成装配后就立即送到守城部队，用于城市保卫战，随后，设计师a·i.苏达列夫根据战场使用情况不断进行改进，战斗结束时，一支全新的冲锋枪诞生了，1943年，该冲锋枪定型号为pps-43式冲锋枪。
第二次世界大战结束后，由二战老兵卡拉什尼柯夫设计的ak47自动步枪正式研制成功，并很快装备部队，冲锋枪便逐步退出苏军装备序列，到1950年代初期，冲锋枪就只用于部队训练了，到1950年代中、晚期，冲锋枪便完全退出苏军装备序列，由ak47自动步枪取代。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条