1) lipophilic degree
亲油化度
1.
The prepared samples are investigated by the lipophilic degree test,FTIR and TEM.
采用亲油化度实验、红外光谱、透射电镜等手段表征了纳米二氧化钛的改性效果和结构。
2.
The results showed that stearic acid was the best modifying agent and optimal condition was 10% dosage,pH 7 and 2 h,its lipophilic degree was up to 89.
实验结果表明,以硬脂酸为改性剂、用量为15%、pH值为8、改性时间为2 h时,改性后的纳米Fe2O3的亲油化度达到89。
3.
Using sodium laurate as modifying agent in the optimal condition ,the lipophilic degree of modified nanometer ZnO is 79.
5h时 ,改性后的纳米ZnO的亲油化度达到 79。
2) Lipophilicity
亲油化度
1.
The lipophilicity of the nanometer CeO2 which is modificated under optimum .
改性后的纳米CeO2的亲油化度达到0。
2.
The modified CaCO3 shows good lipophilicity of 85.
结果表明:以月桂酸钠为改性剂,用量为10％,pH值为7,改性时 间为1h时,改性后的纳米CaCO3的亲油化度达到85。
3) The degree of oil-affinity
亲油化度
1.
The effect of modification is characterized by the degree of oil-affinity and the water-sorption rate.
用亲油化度和吸水率表征改性效果。
4) degree of oil-wetting
亲油程度
5) oil-wetness
亲油度
6) lipophilic chain length
亲油链长度
1.
Surface modifiers with different lipophilic chain lengths,such as lauric acid diethanolamine,myristic acid diethanolamine,palmitic acid diethanolamine and stearic acid diethanolamine,were used to prepare four kinds of LaF3 nanoparticles in the mixture solvent of water-ethanol.
以亲油基链长度不同的十二酸二乙醇胺、十四酸二乙醇胺、十六酸二乙醇胺及十八酸二乙醇胺为表面修饰剂,在醇-水体系中制备了4种纳米氟化镧粒子,通过透射电镜(TEM)、红外光谱(FTIR)、热重仪(TG)研究了纳米氟化镧粒子的形貌及表面修饰情况,利用四球机研究了亲油链长度对纳米氟化镧粒子的摩擦学性能及对基础油感受性的影响。
补充资料：基团亲水亲油平衡数
分子式：
CAS号：
性质： 若将表面活性剂之HLB值看作是构成该表面活性剂分子各基团贡献之总和，则各基团对HLB之贡献称为基团HLB数。根据基团HLB数计算表面活性剂的HLB值时要按照一定的经验公式进行。
CAS号：
性质： 若将表面活性剂之HLB值看作是构成该表面活性剂分子各基团贡献之总和，则各基团对HLB之贡献称为基团HLB数。根据基团HLB数计算表面活性剂的HLB值时要按照一定的经验公式进行。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条