1) fluidizing chlorination slag
沸腾氯化渣
1.
In allusion to the process of titanium white powder produced by chloride giving rise to a large number of fluidizing chlorination slag,which will cause the serious environmental problems if it was directly stacked.
针对氯化法钛白粉生产过程中,产生大量沸腾氯化渣,直接堆放造成环境污染严重的问题。
2) boiling chlorination
沸腾氯化
1.
After comparison of two preparation ways of titanium material by boiling chlorination from Panzhihua ilmenite concentrate and synthetic rutile by hydrochloric acid leaching by fluidization,and in light of the development trend of international titanium materials,an available technology was recommended for possessing Panzhihua natural resources.
比较了攀枝花钛铁矿精矿盐酸法制取人造金红石、流态化法制取适合沸腾氯化用的高品质钛原料两条技术路线的特色,并结合国际钛原料发展趋势,提出了适合沸腾氯化的攀枝花资源高品质富钛料方案。
3) boling chloridizing furnace
沸腾氯化炉
4) boiler slag
沸腾炉渣
1.
Extraction of aluminium and iron from boiler slag by sintering;
用烧结法从沸腾炉渣中提取铝和铁的研究
2.
Extraction of aluminium and iron content from boiler slag by sintering;
烧结法提取沸腾炉渣中的铝和铁
5) fluidized chloridization process
沸腾氯化工艺
6) boiling magnesium chloride solution test for corrosion
沸腾氯化镁试验
补充资料：沸腾氯化镁试验
分子式：
CAS号：
性质：一种评价奥氏体不锈钢应力腐蚀破裂敏感性的标准方法。在42%MgCl2的沸腾溶液中(温度约143℃)，对恒应变或恒载荷的奥氏体不锈钢试件进行浸泡试验。试验周期一般需数百小时。应定期更换溶液并用放大镜观察裂纹引发所需时间。试验后用金相显微镜检查裂纹形貌。该法对奥氏体不锈钢很敏感，对铁素体不锈钢不会产生破裂。
CAS号：
性质：一种评价奥氏体不锈钢应力腐蚀破裂敏感性的标准方法。在42%MgCl2的沸腾溶液中(温度约143℃)，对恒应变或恒载荷的奥氏体不锈钢试件进行浸泡试验。试验周期一般需数百小时。应定期更换溶液并用放大镜观察裂纹引发所需时间。试验后用金相显微镜检查裂纹形貌。该法对奥氏体不锈钢很敏感，对铁素体不锈钢不会产生破裂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。