1) PET/PC blending
PET/PC共混
2) PET/PC blend
PET/PC共混体
1.
The study on the crystallization behaviors of PET/PC blend, an engineering plastics with general high-performance, can provide necessary theory basis for designing and controlling of its properties.
评述了近年来 PET/PC共混体系结晶行为研究的最新工作和理论进展,包括PET/PC共混体系酯交换、相容性及结晶性的关系,退火对 PET/PC共混体系结晶行为的影响,第三组分对PET/PC共混体系结晶行为的影响,PET/PC共混体系结晶动力学以及 PET/PC共混体系高压结晶行为的研究。
3) PC/PET blends
PC/PET共混物
4) PET/PC blends
PET/PC共混体系
1.
The crystallized samples of 20%PC in PET/PC blends mixed at 30 r/min and 523, 533 and 553 K for 15 min were obtained at 300 MPa and 613 K for 6 h with a self-made piston-cylinder high-pressure apparatus.
利用转矩流变仪、DSC、SEM及WAXD等表征手段研究了PET/PC共混体系的酯交换反应对其高压结晶行为的影响。
5) PET/PBT blends
PET/PBT共混
1.
The compatibility of PET/PBT blends has been investigated by differential scanning calorimetry.
结果表明,PET/PBT共混物在非晶区相容而在晶区不相容或部分相容,导电发黑填充PET/PBT合金的渗流阈值为15%,导电炭黑的填充对合金的力学性能有负面的影响。
补充资料：PET
聚对苯二甲酸乙二醇酯是由对苯二甲酸二甲酯与乙二醇酯交换或以对苯二甲酸与乙二醇酯化先合成对苯二甲酸双羟乙酯，然后再进行缩聚反应制得。属结晶型饱和聚酯，平均分子量(2-3)×104，重均与数均分子量之比为1.5-1．8。相对密度1.368．熔点225℃，流动温度243℃：，玻璃化温度80℃，马丁耐热80 ℃，热变形温度98℃(1. 82MPa)，分解温度353℃。具有优良的机械性能．刚性高．硬度大，吸水性很小，尺寸稳定性好。韧性好，耐冲击、耐摩擦、耐蠕变。耐化学性好，溶于甲酚、浓硫酸、硝基苯、三氯醋酸、氯苯酚，不溶于甲醇、乙醇、丙酮、烷烃。使用温度-100～120℃。
弯曲强度 148-310MPa
吸水性 0. 06％-0.129％
冲击强度 64.1-128J／m
洛氏硬度 M 90-95
伸长率 1.8％-2.7％
弯曲强度 148-310MPa
吸水性 0. 06％-0.129％
冲击强度 64.1-128J／m
洛氏硬度 M 90-95
伸长率 1.8％-2.7％