1) PC/PA blend
PC/PA共混物
3) HDPE/PC blend
HDPE/PC共混物
4) PC/PET blends
PC/PET共混物
5) PP/PA blends
PP/PA共混高聚物
1.
By using Instron 1342 testing system and an improved SHPB technique, four kinds of PP/PA blends with two types of interface modifier and different weight ratio are tested at a wide range of strain rates from 10~ -4 up to 10~3 s~ -1 and at a temperature range of 25-80 ℃.
采用Instron1342液压伺服试验机和改进的SHPB技术对2种不同相容剂和重量比的4种PP/PA共混高聚物进行了应变率在10-4～103s-1宽广范围,温度为25℃、40℃、60℃、80℃下的一维应力力学性能试验。
6) PC/LCP blend
PC/LCP二元共混物
1.
The compatibility of PC/LCP blends and the LCP fibrillation can be improved by the addition of small amount of EP resin with low molecular weight and the mechanical properties of the blends were also improved.
在PC/LCP二元共混物中加入少量的低分子量环氧树脂(EP)以改善共混体系的相容性和LCP的成纤能力,从而提高共混物的力学性能。
补充资料：PA/PC blend
分子式：
CAS号：
性质：是PA与PC经适当共混得到的新型高分子材料。具有PC的耐冲击性、耐热性和透明性，也具有PA的优良耐溶剂性、易加工性，还有优良的耐油性、耐应力开裂性、流动性和尺寸稳定性，可加工成大型部件。以SC-70为例，吸水率(23℃水中24h)0.35％，拉伸强度65MPa，弯曲模量300MPa，悬臂梁缺口冲击强度(3.2mm厚)700J/m，热变形温度在1.82MPa负荷下为129℃，0.46MPa下为145℃。PA与PC相容性差，故需加入相容剂，如马来酸酐-烯丙基类接枝共聚物。用机械熔混法制备。可以注塑成型各种制件如电子联结器、继电器、汽车部件及要求耐高温和有机溶剂的制品等。
CAS号：
性质：是PA与PC经适当共混得到的新型高分子材料。具有PC的耐冲击性、耐热性和透明性，也具有PA的优良耐溶剂性、易加工性，还有优良的耐油性、耐应力开裂性、流动性和尺寸稳定性，可加工成大型部件。以SC-70为例，吸水率(23℃水中24h)0.35％，拉伸强度65MPa，弯曲模量300MPa，悬臂梁缺口冲击强度(3.2mm厚)700J/m，热变形温度在1.82MPa负荷下为129℃，0.46MPa下为145℃。PA与PC相容性差，故需加入相容剂，如马来酸酐-烯丙基类接枝共聚物。用机械熔混法制备。可以注塑成型各种制件如电子联结器、继电器、汽车部件及要求耐高温和有机溶剂的制品等。