1) Al-Cr-Ce ternary layers
Al-Cr-Ce三元渗层
1.
Al-Cr binary layers and Al-Cr-Ce ternary layers coatings have been deposited on the surface of martensitic valve steel 4Cr10Si2Mo by solid powder method.
用固体粉末法,在4Cr10Si2Mo马氏体气阀钢表面制备了Al-Cr二元渗层及Al-Cr-Ce三元渗层,研究了渗层的显微组织和成分分布,测定了渗层由表及里的显微硬度。
2) Al-Ti-Ce ternary layers
Al-Ti-Ce三元渗层
1.
Al-Ti binary layers and Al-Ti-Ce ternary layers were prepared on the surface of martensitic valve steel 4Cr10Si2Mo by solid powder method.
用固体粉末法在4Cr10Si2Mo马氏体气阀钢表面制备了Al-Ti二元渗层及Al-Ti-Ce三元渗层,研究了渗层的显微组织和成分分布,测定了渗层显微硬度。
3) Al-Cr-Ce infiltrating
Al-Cr-Ce共渗
4) Al-Cr binary layers
Al-Cr二元渗层
1.
Al-Cr binary layers and Al-Cr-Ce ternary layers coatings have been deposited on the surface of martensitic valve steel 4Cr10Si2Mo by solid powder method.
用固体粉末法,在4Cr10Si2Mo马氏体气阀钢表面制备了Al-Cr二元渗层及Al-Cr-Ce三元渗层,研究了渗层的显微组织和成分分布,测定了渗层由表及里的显微硬度。
5) Ce-Co-Al ternary system
Ce-Co-Al三元系
6) Ce-Al-Cu system
Ce-Al-Cu三元系
1.
Based on the constructed phasecomposition regions of the Ce-Al-Cu ternary system,it reveals that the compositionregion of the bulk glass alloys in the Ce-Al-Cu system falls in the Ce-rich phase regionswithα-Ce_3Al as the common phase.
与Ce-Al-Cu三元系平衡相图相比较而言,对传统电弧熔炼得到的熔铸态样品的相成份确定,可以为非晶金属塑料(AMP)的形成机制提供更好的数据信息。
补充资料：Al
元素符号： al 英文名： aluminum 中文名： 铝
相对原子质量： 26.9815 常见化合价： +3 电负性： 1.61
外围电子排布： 3s2 3p1 核外电子排布： 2,8,3
同位素及放射线： al-26[730000y] *al-27 al-28[2.3m]
电子亲合和能： 48 kj·mol-1
第一电离能： 577.6 kj·mol-1 第二电离能： 1817 kj·mol-1 第三电离能： 2745 kj·mol-1
单质密度： 2.702 g/cm3 单质熔点： 660.37 ℃ 单质沸点： 2467 ℃
原子半径： 1.82 埃 离子半径： 0.51(+3) 埃 共价半径： 1.18 埃
常见化合物： al2o3 alcl3 al2s3 naalo2 al2(so4)3 al(oh)3
发现人： 厄斯泰德、维勒 时间： 1825 地点： 丹麦
名称由来：
拉丁文：alumen， aluminis（铝）。
元素描述：
柔软轻质的银白色金属，在地壳中含量第三。
元素来源：
自然界完全没有铝单质存在。可以电解铝土(al2o3)制取铝。
元素用途：
上自飞机下到易拉罐应用广泛。因为纯铝太柔软，所以要加入不到1%的硅或铁以加大其硬度和强度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条