2) simulating corrosion pits
模拟点蚀坑
1.
Fatigue crack initiation and propagation behavior of the plasma hardened steam turbine last stage blades steel 1Cr12Ni2W1Mo1V were investigated by use with simulating corrosion pits samples.
采用模拟点蚀坑试样,研究了等离子淬火不同温度回火1Cr12Ni2W1Mo1V钢疲劳裂纹萌生和扩展行为。
3) Crater Model
弹坑模型
4) model of gallery
坑道模型
5) pitting
[英]['pitiŋ] [美]['pɪtɪŋ]
坑蚀
1.
The corrosion failure of Ni-P alloy plating was mainly caused by pitting and the process can be divided into initial stage of corrosion,propagation stage and penetration stage of pitting.
596μm;阻抗谱测量结果表明,Ni-P镀层的腐蚀行为主要为坑蚀破坏,可分为腐蚀初期、坑蚀发展和坑蚀深入三个阶段。
2.
The result indicates that electrochemical corrosion,pitting,turbulence and erosion corrosion and their interaction are the main causes of the perforating and leaking of the tubes.
结果表明,空冷器管束在失效环境中发生了腐蚀减薄和穿孔泄漏的主要原因是电化学腐蚀、坑蚀、湍流腐蚀和冲蚀以及他们的交互作用引起的。
6) pitting corrosion
坑蚀
1.
Effect of pitting corrosion on flexural performance of RC beams;
钢筋坑蚀对混凝土梁抗弯性能的影响
2.
Influence of pitting corrosion on the bending capacity of reinforced concrete beams
坑蚀对钢筋混凝土梁抗弯承载力的影响
3.
Also,the influences of the capillary structure to chloride ion permeability and reinforcement localized corrosion(namely pitting corrosion) are pointed out.
指出混凝土毛细孔结构对氯离子渗透和钢筋局部腐蚀(坑蚀)的影响。
补充资料：蚀坑
etchpit：精细抛光的金属表面上由于深度化学蚀刻而形成的有规则形状的小坑。