1) L12 structure Ni3Al
L12结构Ni3Al
2) Ni_3Al
Ni3Al
1.
Cr_3C_2/ Ni_3Al composite is a potential candidate for elevated temperature surface hardfacing material.
Cr3C2/Ni3Al复合材料是一种极具潜力的高温表面耐磨堆焊材料,焊接性对于该材料的推广应用至关重要。
2.
The research and development on formation of Ni_3Al intermetallic compounds by mechanical alloying are presented.
本文综述了用机械合金化法制备金属间化合物Ni3Al的研究现状和发展情况。
3.
When the welding wires were welded on the surface of carbon steel, carbide particles reinforced Ni_3Al base composite was formed due to the physical heat of arc and Ni-Al exothermic reaction.
分析表明,在堆焊过程中,利用氩弧物理热和Ni-Al反应热,Ni与Al化合反应生成Ni3Al金属间化合物,Cr3C2则发生分解,除少部分[C]与[Cr]固溶于Ni3Al基体中外,大部分反应析出更稳定的Cr7C3相,其尺寸取决于堆焊层中不同区域的冷却环境,较为均匀地分布于Ni3Al基体中。
3) Ni 3Al
Ni3Al
1.
A Ni 3Al(Cr) base microcrystalline alloy, strengthened and stabilized by M 3B 2 boride particles, was designed and prepared.
提出将金属间化合物与快速凝固微晶材料的制备工艺结合起来开发新型材料的思路 ,制备出以Ni3Al(Cr)为基 ,用 M3B2 颗粒增强和稳定的 ,具有均匀亚微米尺度的原位复合微晶合金 。
4) L1 2-Al 3Zr phase
L12-Al3Zr
5) L12/L7 E
L12/L7E
6) Ni3Al base
Ni3Al基
1.
The isothermal oxidation behavior of a Ni3Al base alloy containing high contents of W and Mo at 1050℃ was studied.
研究了一种高W、Mo的Ni3Al基合金的1050℃静态抗氧化行为,并采用扫描电镜对不同时间氧化后合金的氧化层形貌进行分析,利用X射线衍射仪分析氧化产物的种类和数量,氧化动力学研究表明,合金的氧化动力学曲线不遵循抛物线规律,以W代Mo,能一定程度上改善高Mo的Ni3Al基合金的1050℃抗氧化性能。
补充资料：[3-(aminosulfonyl)-4-chloro-N-(2.3-dihydro-2-methyl-1H-indol-1-yl)benzamide]
分子式：C16H16ClN3O3S
分子量：365.5
CAS号：26807-65-8
性质：暂无
制备方法：暂无
用途：用于轻、中度原发性高血压。
分子量：365.5
CAS号：26807-65-8
性质：暂无
制备方法：暂无
用途：用于轻、中度原发性高血压。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条