1) Ni3Al superalloy
Ni3Al高温合金
2) Ni3Al base superalloy
Ni3Al基高温合金
1.
The microstructure of Ni3Al base superalloy with composition of Ni-10Co-7.
008CNi3Al基高温合金的显微组织。
3) Ni 3Al alloy
Ni3Al合金
1.
Positron lifetime parameters have been measured by position annihilation technique in binary Ni 77 Al 23 and Ni 74 Al 26 alloys with different Al contents and Ni 3Al alloy doped with different amounts of Zr.
利用正电子湮没技术 (PAT)测量了不同化学计量比二元Ni3Al合金及不同Zr含量Ni3Al合金的正电子寿命谱 ,并估算了合金基体和晶界缺陷处的自由电子密度 。
4) Ni3Al based alloy
Ni3Al基合金
1.
The effect of silicon on microstructure of the directionally solidified Ni3Al based alloy IC6A was studied using scanning electron microscopy(SEM), transmission electron microscopy(TEM), energy dispersive spectroscopy(EDS), electron probe micro analysis(EPMA) and X ray diffractometry.
利用扫描电镜(SEM)、透射电镜(TEM)、电子探针(EPMA)、能谱(EDS)和X射线衍射(XRD)技术研究了硅对定向凝固Ni3Al基合金IC6A微观组织的影响。
5) Ni3Al-Mo alloy
Ni3Al-Mo合金
6) Ni_3Al/graphite alloy
Ni3Al/石墨合金
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)