1) belite-barium calcium sulphoaluminate
贝利特-硫铝酸钡钙
1.
The influence of gypsum on compressive strength and performance of hardened paste of belite-barium calcium sulphoaluminate cement was studied.
研究了石膏对贝利特-硫铝酸钡钙水泥强度和硬化浆体结构的影响。
2) belite-barium calcium sulphoaluminate cement
贝利特-硫铝酸钡钙水泥
1.
The mechanical properties of belite-barium calcium sulphoaluminate cement and its composition and structure of the hydration products are studied by compressive strength test,XRD,and SEM under different curing temperature for 5℃,20℃ and 35℃,respectively.
通过力学性能测试、XRD及SEM分析,研究在5℃、20℃和35℃养护温度下贝利特-硫铝酸钡钙水泥的力学性能和水化产物的组成和结构,并与普通硅酸盐水泥及贝利特水泥进行比较。
3) alite-barium calcium sulphoaluminate cement
阿利特-硫铝酸钡钙水泥
1.
The effects of the composition of clinker minerals,gypsum content and environment temperature on the slurry rheological and dry shrinkage properties of alite-barium calcium sulphoaluminate cement were studied.
结果表明:阿利特—硫铝酸钡钙水泥的新拌浆体属于Bingham型流体,水泥浆体的屈服应力和黏度受熟料中硫铝酸钡钙矿物含量变化的影响较大,随石膏掺量的增加和环境温度的增高而减小;阿利特-硫铝酸钡钙水泥具有一定的微膨胀性能,其砂浆的干缩性能优于硅酸盐水泥砂浆。
2.
Experimental results show that when the slag content is 10% the compressive strength of alite-barium calcium sulphoaluminate cement reachs 44.
研究矿渣掺量对阿利特-硫铝酸钡钙水泥性能的影响,当质量分数掺量为10%时,阿利特-硫铝酸钡钙水泥3 d、28 d的强度分别达到44。
3.
The drying shrinkage and mechanical property of alite-barium calcium sulphoaluminate cement (SABC) mortars were investigated by contrasting with Portland cement mortars.
通过与硅酸盐水泥(portland cement,PC)对比,研究了阿利特-硫铝酸钡钙水泥(alite-barium calcium sulphoaluminate cement,SABC)砂浆的力学性能和干缩性能。
4) alite-calcium barium sulphoaluminate cement
阿利特-硫铝酸钡钙水泥
1.
The influence of different contents of slag,fly ash and zeolite powers on the strength of alite-calcium barium sulphoaluminate cement mortar is investigated,and the reaction mechanism is discussed.
研究不同掺量的矿渣、粉煤灰和沸石粉对阿利特-硫铝酸钡钙水泥砂浆强度的影响规律,并对其反应机理进行探讨。
2.
Effects of slag on the structure and properties of cement pastes were studied by determining the setting time, the mechanical property and pore structure of hardened Alite-Calcium Barium Sulphoaluminate cement pastes, and using scanning electron microscopy and DTA-TG.
通过对水泥浆体凝结性能、力学性能和孔结构的测定,结合扫描电镜分析和差热-热重分析,研究了矿渣掺量对阿利特-硫铝酸钡钙水泥浆体硬化浆体结构和性能的影响。
5) Alite-C2.75B1.25A3S cement
阿利特-硫铝酸钡钙水泥
1.
Compared with Portland cement concrete,the impermeability of Alite-C2.
在与相同配合比的普通硅酸盐水泥混凝土的对比试验中,采用抗渗试验和孔结构分析的方法,研究了阿利特-硫铝酸钡钙水泥混凝土的抗渗性能与水灰比的关系。
6) calcium barium sulphoaluminate
硫铝酸钡钙
1.
The synthesis conditions of belite-calcium barium sulphoaluminate cement clinker were studied by the orthogonal test method.
采用正交试验方法研究了贝利特—硫铝酸钡钙水泥熟料的煅烧条件。
2.
Synthesis conditions and mechanical performance of belite-calcium barium sulphoaluminate cement clinker were investigated by the orthogonal test taking clinker modulus and content of calcium barium sulphoaluminate(C_(2.
选择熟料率值和硫铝酸钡钙掺量为影响因素,通过正交试验研究了贝利特—硫铝酸钡钙水泥的合成条件和力学性能,并利用XRD、SEM-EDS等测试手段分析了该水泥熟料的组成和结构。
3.
Belite–calcium barium sulphoaluminate cement is a new type of cementitious material.
贝利特–硫铝酸钡钙水泥是一种新型的水泥材料,通过在贝利特熟料矿物体系中引入硫铝酸钡钙矿物,达到提高贝利特水泥早期强度的目的。
补充资料：贝利特
分子式：
CAS号：
性质：简称B矿。含有少量氧化铝、氧化铁、氧化钠、氧化镁、氧化钾等氧化物的硅酸二钙固溶体。有β、α′和α型。组成：氧化钙63.0%～63.7%，二氧化硅31.5%～33.7%，三氧化二铝1.1%～2.6%，三氧化二铁0.7%～2.2%；其余为氧化镁、氧化钠、氧化钾、二氧化钛、五氧化二磷等。二轴晶晶体折射率ng=1.735，nm=1.726，np=1.717，双折射率ng-np=0.018。硅酸盐水泥熟料中的重要矿物成分，但大多以β型存在于熟料。β型贝利特为单斜晶系，呈棱柱状或板状，在正常熟料中呈圆粒状，能使水泥石后期机械强度缓慢增长，并有抗硫酸盐侵蚀和水化热低的特点。
CAS号：
性质：简称B矿。含有少量氧化铝、氧化铁、氧化钠、氧化镁、氧化钾等氧化物的硅酸二钙固溶体。有β、α′和α型。组成：氧化钙63.0%～63.7%，二氧化硅31.5%～33.7%，三氧化二铝1.1%～2.6%，三氧化二铁0.7%～2.2%；其余为氧化镁、氧化钠、氧化钾、二氧化钛、五氧化二磷等。二轴晶晶体折射率ng=1.735，nm=1.726，np=1.717，双折射率ng-np=0.018。硅酸盐水泥熟料中的重要矿物成分，但大多以β型存在于熟料。β型贝利特为单斜晶系，呈棱柱状或板状，在正常熟料中呈圆粒状，能使水泥石后期机械强度缓慢增长，并有抗硫酸盐侵蚀和水化热低的特点。