1) barium calcium sulphoaluminate cement
硫铝酸钡钙水泥
1.
Applied the basic principles of thermodynamics of materials to estimate solid-phase reaction of clinker free energy to optimize the composition of the clinker mineral,and analyzed belite-barium calcium sulphoaluminate cement sintering process with XRD.
应用材料热力学的基本原理估算熟料固相反应的自由能,进行熟料矿物组成的优化,并利用XRD分析了贝利特-硫铝酸钡钙水泥的煅烧过程。
2) alite-barium calcium sulphoaluminate cement
阿利特-硫铝酸钡钙水泥
1.
The effects of the composition of clinker minerals,gypsum content and environment temperature on the slurry rheological and dry shrinkage properties of alite-barium calcium sulphoaluminate cement were studied.
结果表明:阿利特—硫铝酸钡钙水泥的新拌浆体属于Bingham型流体,水泥浆体的屈服应力和黏度受熟料中硫铝酸钡钙矿物含量变化的影响较大,随石膏掺量的增加和环境温度的增高而减小;阿利特-硫铝酸钡钙水泥具有一定的微膨胀性能,其砂浆的干缩性能优于硅酸盐水泥砂浆。
2.
Experimental results show that when the slag content is 10% the compressive strength of alite-barium calcium sulphoaluminate cement reachs 44.
研究矿渣掺量对阿利特-硫铝酸钡钙水泥性能的影响,当质量分数掺量为10%时,阿利特-硫铝酸钡钙水泥3 d、28 d的强度分别达到44。
3.
The drying shrinkage and mechanical property of alite-barium calcium sulphoaluminate cement (SABC) mortars were investigated by contrasting with Portland cement mortars.
通过与硅酸盐水泥(portland cement,PC)对比,研究了阿利特-硫铝酸钡钙水泥(alite-barium calcium sulphoaluminate cement,SABC)砂浆的力学性能和干缩性能。
3) barium-bearing calcium sulfo-ferritealuminate
硫铁铝酸钡钙水泥
4) alite-calcium barium sulphoaluminate cement
阿利特-硫铝酸钡钙水泥
1.
The influence of different contents of slag,fly ash and zeolite powers on the strength of alite-calcium barium sulphoaluminate cement mortar is investigated,and the reaction mechanism is discussed.
研究不同掺量的矿渣、粉煤灰和沸石粉对阿利特-硫铝酸钡钙水泥砂浆强度的影响规律,并对其反应机理进行探讨。
2.
Effects of slag on the structure and properties of cement pastes were studied by determining the setting time, the mechanical property and pore structure of hardened Alite-Calcium Barium Sulphoaluminate cement pastes, and using scanning electron microscopy and DTA-TG.
通过对水泥浆体凝结性能、力学性能和孔结构的测定,结合扫描电镜分析和差热-热重分析,研究了矿渣掺量对阿利特-硫铝酸钡钙水泥浆体硬化浆体结构和性能的影响。
5) Alite-C2.75B1.25A3S cement
阿利特-硫铝酸钡钙水泥
1.
Compared with Portland cement concrete,the impermeability of Alite-C2.
在与相同配合比的普通硅酸盐水泥混凝土的对比试验中,采用抗渗试验和孔结构分析的方法,研究了阿利特-硫铝酸钡钙水泥混凝土的抗渗性能与水灰比的关系。
6) belite-barium calcium sulphoaluminate cement
贝利特-硫铝酸钡钙水泥
1.
The mechanical properties of belite-barium calcium sulphoaluminate cement and its composition and structure of the hydration products are studied by compressive strength test,XRD,and SEM under different curing temperature for 5℃,20℃ and 35℃,respectively.
通过力学性能测试、XRD及SEM分析,研究在5℃、20℃和35℃养护温度下贝利特-硫铝酸钡钙水泥的力学性能和水化产物的组成和结构,并与普通硅酸盐水泥及贝利特水泥进行比较。
补充资料：阿利
| 阿利（1885～1955） Allee，Warder Clyde 美国动物学家。1885年6月5日生于美国印第安纳州布卢明顿附近，1955年3月18日卒于佛罗里达。1908 年在印第安纳的厄勒姆学院获学士学位，1910年和1912年在芝加哥大学先后获硕士学位和博士学位。1910年任该校动物学助教，1914年为俄克拉何马城大学副教授。1915年为雷克福里斯特学院教授。1921年任芝加哥大学副教授，1925年任教务长，1928年任教授，1950年后为名誉退职教授。1950～1955年为佛罗里达大学生物学教授会主任。他是美国生态学家V.E.谢尔福德的学生，早年研究池塘动物群落演替，随后研究海洋无脊椎动物生态学。他一生以研究动物的社会行为和集群而闻名。著有《动物的集群》、《动物的生活和社会增长》、《动物的社会生活》等书。他发现集群能提高动物的存活力，生态学中的阿利规律，说明中等的适当密度对种群最有利的原理 。1949年以阿利为首的5个生态学家合编的《动物生态学原理》一书的出版标志着动物生态学已成熟为一门独立的学科。1929年，阿利任美国生态学会主席。1942年为美国科学促进协会会员，美国昆虫学会会员、美国科学和技术科学院院士。1930～1955年他一直任《生理动物学》杂志的主编。1944～1950年任《不列颠百科全书》动物学方面论文的校订委员会主席。 |