1) PMR polyimides
PMR型聚酰亚胺树脂
1.
PMR polyimides with asymmetric biphenylimide chain segments were prepared by using diethylester of 2,3,3\',4\'-biphenyltetracarboxylic dianhydride,the mixture of p-phenylenediamine and m-phenylenediamine,as well as monoethylester of 5-norbornene-2,3-dicarboxylic acid as endcaping agent.
采用活性单体原位聚合方法,由2,3,3\',4\'-联苯四甲酸二乙酯为芳香族二酸二酯、对苯二胺与间苯二胺混合物为芳香族二胺、降冰片稀二甲酸单乙酯为反应性封端剂制备了系列PMR型聚酰亚胺树脂。
3) PMR-polyimide
PMR聚酰亚胺
4) Polyimide
[英][,pɔli'imaid] [美][,pɑli'ɪm,aɪd]
聚酰亚胺树脂
1.
The curing kinetics of phenylethynyl terminated polyimide;
苯乙炔基封端聚酰亚胺树脂的固化动力学研究
5) polyimide resin
聚酰亚胺树脂
1.
Study on curing kinetic parameter for polyimide resin;
聚酰亚胺树脂固化动力学参数研究
2.
The paper introduces polyimide resin and its wheel's manufacturing and application.
聚酰亚胺树脂是一种耐高温、高强度的工程塑料。
3.
In this paper, a polyimide resin micropowder which is used as a new kind of resinoid bond of diamond optical polishing pills is presented.
本文介绍了聚酰亚胺树脂粉在金刚石抛光片中的应用。
6) PPTA
聚苯酰亚胺树脂
1.
Synthesis of the New Stationary Phase for High Performance Liquid Affinity Chro-matography with Dendritic Spacer Arm Using Poly (p-Phenyleneterephthalamide) (PPTA) as the Matrix;
以聚苯酰亚胺树脂微球为基体的树状间隔臂亲和色谱固定相的合成
补充资料：PMR型聚酰亚胺
分子式：
CAS号：
性质：又称PMR型聚酰亚胺，一类重要的高性能复合材料基体树脂。单体在材料制备和成型过程中完成聚合反应。主要品种有PMR-15、PMR-Ⅱ、LARC-160和LARC-13等。可由内次甲基四氢化邻苯二甲酸(NA酸酐)单烷基酯、芳族四羧酸二甲酯、与芳族二元胺按一定比例反应，得到溶于低级醇的预聚物。然后，纤维预浸料在200℃进一步聚合和环化，生成内亚甲基四氢化邻苯二甲酰亚胺(Nad-酰亚胺)封端的聚酰亚胺。Nad-酰亚胺在300℃以上经逆Diels-Alder反应，裂解为环戊二烯和马来酰亚胺端基，同时进行双键加成反应形成交联体系。PMR聚酰亚胺碳纤维复合材料具有优良的综合性能，可在250～300℃长期使用。用作飞机发动机的轴承、外罩、喷管、机舱、涡轮机叶片、机翼、导弹壳体等。
CAS号：
性质：又称PMR型聚酰亚胺，一类重要的高性能复合材料基体树脂。单体在材料制备和成型过程中完成聚合反应。主要品种有PMR-15、PMR-Ⅱ、LARC-160和LARC-13等。可由内次甲基四氢化邻苯二甲酸(NA酸酐)单烷基酯、芳族四羧酸二甲酯、与芳族二元胺按一定比例反应，得到溶于低级醇的预聚物。然后，纤维预浸料在200℃进一步聚合和环化，生成内亚甲基四氢化邻苯二甲酰亚胺(Nad-酰亚胺)封端的聚酰亚胺。Nad-酰亚胺在300℃以上经逆Diels-Alder反应，裂解为环戊二烯和马来酰亚胺端基，同时进行双键加成反应形成交联体系。PMR聚酰亚胺碳纤维复合材料具有优良的综合性能，可在250～300℃长期使用。用作飞机发动机的轴承、外罩、喷管、机舱、涡轮机叶片、机翼、导弹壳体等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。