1) melting combination
熔融组合
2) fusing together method
组合熔融法
3) melt polymerization
熔融聚合
1.
Study on improvement of melt polymerization of polylactic acid;
聚乳酸的熔融聚合法的改进研究
2.
Synthesis and characterization of polyglycollic acid via direct melt polymerization;
直接熔融聚合聚乙醇酸的合成与表征
3.
Based on the synthetic research, using PTA, 1,3-PDO as raw materials, 300L PTT melt polymerization with Ti/Sb/Co/P composite catalyst system was carried out.
以PTA、1,3-PDO为原料,在小试合成研究的基础上,采用Ti/Sb/Co/P复合催化体系进行了300L釜规模的PTT熔融聚合研究,并研究了PTT产品的物理机械性能。
5) melt polycondensation
熔融聚合
1.
Study on synthesis of biodegradable material poly(Lactic Acid-co-Alaine) via melt polycondensation;
熔融聚合法合成生物材料聚(乳酸-丙氨酸)
2.
Staring from D,Llactic acid, poly(DLlactic acid) (PDLLA) was directly synthesized through melt polycondensation.
以DL-乳酸为原料,通过熔融聚合法直接合成外消旋聚乳酸(PDLLA)。
3.
Though the relative molecular mass of polylactic acids via solution polycondensation is higher than that via melt polycondensation, the latter is simpler in process, and is suitable to synthesize the extension prepolymer for further advancing relative molecular mass.
其中 ,溶液聚合可以比熔融聚合获得相对较高的相对分子质量 ,但熔融聚合法较溶液聚合法的工艺更简单 ,适宜于制备扩链反应的预聚体。
补充资料：熔融
分子式：
CAS号：
性质：温度升高时，分子的热运动能增大，导致结晶破坏，物质由晶相变为液相的过程。熔融是一级相转变，熔融有热焓、熵和体积的增大。发生熔融的温度叫熔点或熔融温度。小分子晶体的熔点温度范围很窄（一般小于1℃），而聚合物由于结晶不完全；其熔融温度往往是一个较宽的范围（一般为10～20℃）。
CAS号：
性质：温度升高时，分子的热运动能增大，导致结晶破坏，物质由晶相变为液相的过程。熔融是一级相转变，熔融有热焓、熵和体积的增大。发生熔融的温度叫熔点或熔融温度。小分子晶体的熔点温度范围很窄（一般小于1℃），而聚合物由于结晶不完全；其熔融温度往往是一个较宽的范围（一般为10～20℃）。