2) Tungsten Oxide Films
三氧化钨薄膜
1.
In the text, the tungsten oxide films were prepared with sol-gel and reactive magnetron sputtering methods.
本文采用反应磁控溅射法和溶胶凝胶法制备了均匀致密的三氧化钨薄膜材料,对它的光学性质、表面形态、结构等进行了深入的研究。
2.
Study on the Property and Mechanism Sensitive to Hydrogen of Tungsten Oxide Films Doped Catalyst;
由于三氧化钨薄膜在常温下对氢气不敏感,本文采用掺杂改性来改善三氧化钨薄膜材料的氢敏性能,分别采用直流磁控溅射法和溶胶凝胶法制备了均匀的三氧化钨掺铂和掺钯薄膜材料,并对它的光学性质、表面形态、结构等进行了深入的研究。
3) tungsten oxide thin film
氧化钨薄膜
1.
X-ray photoelectron spectrum (XRS) show that there are three main kinds of stoichiometry tungsten oxide in tungsten oxide thin film prepared by r.
由于薄膜沉积过程中缺乏氧气,溅射得到的是化学配比偏离WO3的氧化钨薄膜,本文详细研究了不同电压下,R。
4) porous tungsten oxide film
三氧化钨多孔薄膜
5) tungsten titanium oxide film
氧化钨钛薄膜
6) WO3-MoO3 thin film
氧化钨钼薄膜
1.
The electrochemistry impedance spectroscopies of ITO plane electrodes and ITO plane electrodes with Ni doped WO3-MoO3 thin film immersed in 1 mol NaCl electrolyte were studied by means of the equivalent circuits.
用溶胶凝胶的方法在ITO导电基片上制备了一组不同掺镍量的氧化钨钼薄膜,分别测量了该系统及ITO电极浸泡于1 mol氯化钠溶液中不同频率下的电化学阻抗,应用等效电路法模拟了该系统的阻抗谱,从而获得了有关掺镍薄膜的电阻、电容及溶液在薄膜内扩散等信息。
补充资料：三氧化钨
W03 分子量231．85
淡黄色斜方晶系结晶粉末。加热时颜色由浅变深。密度7．16g/cm3。熔点1473℃。熔融时呈绿色。沸点1750℃。850℃时显著升华。不溶于水和除氢氟酸外的无机酸，能缓馒的溶于氨水或浓碱溶液。与氯气加热反应生成氯氧化物，但不能与溴、碘反应。
应用领城 用于硬质合金、刀具和模具的制造。也可用于制造金属钨、拉钨丝，制备X-射线屏和防火织物。还可用作黄色陶瓷器的着色剂。
淡黄色斜方晶系结晶粉末。加热时颜色由浅变深。密度7．16g/cm3。熔点1473℃。熔融时呈绿色。沸点1750℃。850℃时显著升华。不溶于水和除氢氟酸外的无机酸，能缓馒的溶于氨水或浓碱溶液。与氯气加热反应生成氯氧化物，但不能与溴、碘反应。
应用领城 用于硬质合金、刀具和模具的制造。也可用于制造金属钨、拉钨丝，制备X-射线屏和防火织物。还可用作黄色陶瓷器的着色剂。