1) thermo-compression drift
热压冲头
1.
The failure reason of the thermo-compression drift was analyzed through macroscopic examination, hardness testing and metallographic examination.
利用宏观检验、硬度测试及金相检验等方法,对热压冲头失效原因进行分析。
2) Failure Analysis of Thermo-compression Drift
热压冲头失效分析
3) Plunger
[英]['plʌndʒə(r)] [美]['plʌndʒɚ]
压射冲头
1.
The life of the BeCu plunger is 2.
铍铜压射冲头的使用寿命是球铁压射冲头的２。
4) flushing pressure head
冲压头
1.
This essay introduceds the design method of the flushing pressure head with a rectangular hole that distributes according to certain rule and that is used for blanking, the ramming mold as well as the necessary equipment that can adjusts the position.
介绍了用于冲裁按一定规律分布的,矩形孔的冲压头、冲压模具以及配套调位机构的设计方法,对该装置的总体结构、特点及工作过程进行了阐述。
5) Compression casting plunger
压铸冲头
6) bumped head
冲压封头
补充资料：热压
热压
hot pressing
reyo热压(hot pressing)一种将模压与烧结相结合的成形方法，又称静热压(statie hot pressing)、加压烧结，也称活化烧结。它是将金属粉末装在模腔内，平稳地加压同时将粉末加热到正常的烧结温度或稍低一些的温度，经过较短的时间，烧结成致密而均匀的制品。为了使预热粉末或预压压坯不被空气氧化或氮化，热压过程必须在保护气氛或真空下进行。热压模的选择原则一般是:低温高压工艺可选择金属或硬质合金模;高温高压工艺则选择石墨模。尽管人们对加压烧结和热压这两个术语交叉使用，但这两个工艺过程却各有侧重。在加压烧结中，强调的是热过程;在热压中则着重强调施加的压力是主要的可调变量。热压技术的特点是:粉末致密化以及脱模所用的设备和工序与冷压和烧结工艺无区别，所不同的是热压时间较长，即在特定的压力及温度下，通过塑性变形、蠕变及扩散使粉末压坯充分密实所需的时间较长，因此生产率降低，成本较高。但由于热压工艺可大大降低成形压力(为冷压成形的十分之一)，缩短烧结时间，制造密度极高、晶粒极细的材料，它们常用来制造硬质合金及陶瓷刀具、拉丝模及大型、异形薄壁管、薄片，还可以压制硬而脆的碳化硼及陶瓷制品。 在密闭模中热压金属粉末是粉末冶金方法中最古老的方法之一。1912年和1917年德国和美国分别获得了钨和碳化钨粉热压制造致密件的专利，1920年以后欧洲和美国生产了圆柱形的拉丝模，从1930年起热压技术发展更快。近年来又发展了真空热压和振动热压，为了提高生产率还研制出实现连续热压的竖式和卧式连续热压机。 (张齐勋)