2) the curly elasticity
卷曲弹性率
3) fibre crimp elasticity metre
纤维卷曲弹性仪
4) crimp recovery rate
卷曲弹性回复率
1.
As the tension of the heat treatment rose,the crimp frequency and the crimp radius of the monofilament went down,the crimp elongation rate went down,the crimp recovery rate and the crimp modulus of the monofilament and multifilament went up.
结果表明:随着热处理张力的增加,单丝的卷曲数和卷曲半径减小,单丝和复丝的卷曲伸长率减小,卷曲弹性回复率增加,卷曲模量增加;随着热处理温度的增加,单丝的卷曲数增加,卷曲半径减小,单丝和复丝的卷曲伸长率减小,卷曲弹性回复率增加,卷曲模量增加;在温度100～120℃且张力较小的条件下进行热处理时,PET/PTT纤维的单丝和复丝的卷曲弹性较好。
5) crimp property
卷曲性
1.
The thesis analysis is made on the crimp property of polyester/modified high shrinkage polyester conjugated fiber.
对聚酯/改性高收缩聚酯复合纤维的卷曲性能进行了理论分析,并测试了不同组分比例以及不同热处理方式、温度、时间条件下的聚酯/改性高收缩聚酯复合纤维的卷曲性能。
6) crimp property
卷曲性能
1.
The crimp property and mechanism of sidc-by-side composite polyamide fibre based on various combinations: Nylon 6 and Nylon 66 with copolyamide (1) and co-polyamide (2) were investigated in this paper, taking into account of factors that affected the crimp property.
本文着重探讨了尼隆类复合纤纷的卷曲性能和卷曲机理以及影响卷曲性能的各种因素。
2.
Side-by-side PET/PTT bi-component filaments at 50/50 weight ratio were produced under normal industrial conditions and the effects of different drawing technological parameters including draw ratio,temperatures of hot disc and hot plate on the boiling shrinkage property and crimp property of PTT/PET bi-component filaments were systematically investigated.
研究了牵伸工艺参数,包括不同牵伸比、热盘和热板温度对并列型50/50 PET/PTT复合长丝的沸水收缩性能和卷曲性能的影响。