2) hot dip aluminizing
热浸渗铝
1.
The hot dip aluminizing process at 760~800 ℃ for 30~50 min and diffusion annealing at 900 ℃ for 3~5 h in parts of valve disc are applied to improve the anti-oxidation ability of the disc.
对闸板局部进行了(760~800)℃×(30~50)m in热浸渗铝和900℃×(3~5)h扩散退火,提高了闸板的抗高温氧化性能,使热风阀的平均使用寿命由4年延长到8年以上。
3) hot-dip aluminizing
热浸渗铝
1.
Effect of rare-earth elements added in hot-dip aluminizing liguid has been studied on the diffusion coe-fficient of aluminum during hot-dip aluminizing for low carbon steel.
研究了热浸渗铝液中添加微量稀土元素对低碳钢热浸渗铝时铝的扩散系数的影响,结果表明,稀土元素能增大铝原子的扩散激活能,降低铝原子的扩散系数。
4) aluminum diffusion
扩散渗铝
1.
The aluminized graphite electrodes were obtained by spray coating method and an appropriate heat treatment for aluminum diffusion.
为了提高石墨电极的使用寿命,避免电极燃烧部位掉进炼钢炉增加钢的含碳量,从而降低钢的质量,本文研究开发了电极表面的热喷涂扩散渗铝工艺,利用该工艺制备的涂层电极,在间隙式电炉中炼钢时,降低电极单耗20%～30%,吨钢节约电极费用5～10元。
5) hot-dipped aluminum
热浸镀渗铝
1.
Technique of hot-dipped aluminum steel sample preparation for TEM;
热浸镀渗铝钢TEM制样技术
6) hot dip aluminized steel
热浸渗铝钢
补充资料：热浸
分子式：
分子量：
CAS号：
性质：或称热搪。将较不活泼金属的制件浸在熔融的较活泼金属中而形成覆盖层的方法。可以减缓或防止腐蚀。两种金属须能生成二元合金。例如铁制件可在熔融的铝、锡或锌中进行热浸。往往加入第三种金属生成三元合金。例如铁不能与铅生成合金，但可在熔融的铅和锡中进行热浸。优点是：（1）操作和设备简单；（2）效果比电镀好。缺点是：（1）覆盖层较厚；（2）不规则的制件不容易形成均匀的膜；（3）只适于用低熔点金属（锌、锡、铝、铅）覆盖。