1) non-soap seed emulsion polymerization
无皂种子乳液聚合
1.
P(St-EA-MAA) copolymer latex was synthesized by a half continuous non-soap seed emulsion polymerization using styrene(St) as a skeleton,ethyl acrylate ester(EA) and methyl cyrlic acid(MAA) asmonomers.
利用无皂种子乳液聚合法合成了以聚苯乙烯(St)为骨架、丙烯酸乙酯(EA)和甲基丙烯酸(MAA)为共聚单体的P(St-EA-MAA)共聚物乳液;乳液经碱酸分步处理法制得共聚物多孔微球。
2) seeded soap-free emulsion polymerization
种子无皂乳液聚合
1.
Mono-dispersed PMMA/GMA/DVB(PMGD) microspheres with size ranging from 200 to 800 nm were synthesized by soap-free emulsion polymerization and seeded soap-free emulsion polymerization.
采用无皂乳液聚合及种子无皂乳液聚合方法制备了200～800nm四种不同尺寸的单分散PMMA/GMA/DVB(PMGD)复合微球。
3) soap free cationic emulsion copolymerization
无皂阳离子乳液共聚合
4) soap-free cationic emulsion copolymerization
无皂阳离子乳液聚合
5) soapless seed emulsion polymerization
无皂种子乳液
6) soap-free emulsion polymerization
无皂乳液聚合
1.
Nano silica was modified by soap-free emulsion polymerization using methacrylic acid (MA) and acrylic acid (AA)as monomer;
MA/AA无皂乳液聚合改性纳米SiO_2
2.
Preparation of fluorocarbon polymer emulsion by the method of soap-free emulsion polymerization;
无皂乳液聚合法制备氟碳聚合物乳液
3.
Research on reaction mechanism and preparation methods of soap-free emulsion polymerization;
无皂乳液聚合反应机理和制备方法的研究进展
补充资料：种子乳液聚合
分子式：
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。