说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> 非枝晶组织形成机制
1)  formation mechanism of non-dendrite microstructure
非枝晶组织形成机制
2)  Non-dendritic microstructure
非枝晶组织
3)  Non-dendrite Structure
非枝晶组织
1.
The result showed that, by adopting proper pouring temperature, chilling the molten metal before mould filling, and properly vibrating the supercooled molten metal, it is possible to obtain spheroidal or quasi-spheroidal non-dendrite structure of proeutectic austenite; and, under the condition of low temperature pouring with a slope plate cooler, the molten metal washing, flowing and.
结果表明:通过控制合适的浇注温度,并对充型前的金属液进行激冷处理,同时对过冷的金属液配以适当的振动,可以获得球形或近球形的先共晶奥氏体非枝晶组织;在带有倾斜板冷却体的低温浇注情况下,金属液的冲刷、流动及振动使熔体获得了均匀的溶质场和温度场,抑制了发达的先共晶奥氏体枝晶的形成,为球状晶的获得提供了条件。
4)  Nondendritic structure
非枝晶组织
1.
Semi-solid isothermal treatment is thought as a potential technology in the manufacturing nondendritic structure alloy slurry,the research of this technology is helpful to enrich the theory of semi-solid metal forming and to accelerate the application of this technology.
半固态等温热处理作为一种比较有发展前途的非枝晶组织坯料制备方法,对其展开研究将有助于丰富半固态金属成形理论和加速该技术的工业化应用。
5)  non-dendritic structure
非枝晶组织
1.
The effect of various parameters, for example, stirring intensity, locality and cooling rate etc, on the non-dendritic structure form of Al-6.
6%Si亚共晶合金非枝晶组织形成的影响,并利用图像分析仪对试样单位面积上的颗粒数进行了定量的测量。
2.
This paper introduced the key technology of SSP(semi-soild process) thixomolding of magnesium alloys : the preparation of non-dendritic structure,reheating,thixomolding.
介绍了镁合金半固态触变成形技术中的三个关键技术:非枝晶组织半固态浆料的制备、坯料的二次加热、半固态触变压铸成形。
3.
Semi-solid isothermal treatment is thought as a potential technology in the manufacturing non-dendritic structure alloy slurry, the research of this technology is helpful to rich the theory of semi-solid metal forming and accelerate the application of this technology.
半固态等温热处理作为一种比较有发展前途的非枝晶组织坯料制备方法,对其展开研究将有助于丰富半固态金属成形理论和加速该技术的工业化应用。
6)  non dendritic structure
非枝晶组织
1.
The non dendritic structure for thixo forming could be obtained when ZA27 alloy modified by these elements was heat treatd at semi solid temperature.
结果表明 :Zr的变质效果最好 ,下来依次是 B- Ti、Ti;经半固态等温热处理后都可获得触变成形所需的半固态非枝晶组织 ,但变质组织越细 ,越易获得良好的非枝晶组织 ,变质效果越差 ,需要热处理的时间越长或温度越高。
2.
In this paper, the formation mechanism for non dendritic structure in semi solid metal is proposed, namely mechanism of particle drift and blending compressing.
提出了半固态材料中非枝晶组织的形成机制 ,即“晶粒漂移和混和抑制机制”。