2) seeded soap-free emulsion polymerization
种子无皂乳液聚合
1.
Mono-dispersed PMMA/GMA/DVB(PMGD) microspheres with size ranging from 200 to 800 nm were synthesized by soap-free emulsion polymerization and seeded soap-free emulsion polymerization.
采用无皂乳液聚合及种子无皂乳液聚合方法制备了200～800nm四种不同尺寸的单分散PMMA/GMA/DVB(PMGD)复合微球。
3) non-soap seed emulsion polymerization
无皂种子乳液聚合
1.
P(St-EA-MAA) copolymer latex was synthesized by a half continuous non-soap seed emulsion polymerization using styrene(St) as a skeleton,ethyl acrylate ester(EA) and methyl cyrlic acid(MAA) asmonomers.
利用无皂种子乳液聚合法合成了以聚苯乙烯(St)为骨架、丙烯酸乙酯(EA)和甲基丙烯酸(MAA)为共聚单体的P(St-EA-MAA)共聚物乳液;乳液经碱酸分步处理法制得共聚物多孔微球。
4) soap-free polymerization
无皂聚合
1.
Synthesis and application of soap-free polymerization coat dyeing adhesive
无皂聚合涂料染色粘合剂的合成及应用
2.
The core-shell type surface sizing agent PSS synthesized by introducing a functional monomer in the soap-free polymerization technology was prepared using acrylate, styrene, acrylic acid as raw materials.
以苯乙烯、丙烯酸酯、丙烯酸等为原料,采用功能单体引入法无皂聚合工艺制备了性能稳定的核壳型共聚物表面施胶剂(PSS)。
3.
Acrylic emulsion containing 10% carboxyl was prepared by way of soap-free polymerization.
本工作经无皂聚合制备了羧基含量为10%的丙烯酸乳液。
5) soap free cationic emulsion copolymerization
无皂阳离子乳液共聚合
6) soap-free cationic emulsion copolymerization
无皂阳离子乳液聚合
补充资料：种子乳液聚合
分子式：
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。