1) alumina-magnesia dry ramming mix
铝镁质干式捣打料
1.
Physical properties at room temperature and slag resistance of alumina-magnesia dry ramming mix with different content of boric acid were investigated.
研究了不同硼酸加入量对铝镁质干式捣打料常温物理性能及抗渣性的影响。
2) magnesia ramming materials
镁质捣打料
1.
Using magnesia ramming materials in furnace bottom and partial hear th instead of traditional shaped magnesia bricks can prolong furnace life,reduce r efractories consumptions per one ton product and increase equipment utilization rate.
叙述了中低碳锰铁精炼炉用镁质捣打料在炉底与部分炉缸取代传统的成型镁砖作炉 衬材料，达到了延长炉龄、降低吨产品耐火材料消耗、提高设备作业率的目的。
3) Dry ramming mix
干式捣打料
1.
Effect of the particle size distribution on the properties of dry ramming mix;
粒度分布对干式捣打料性能的影响
4) Magnesite carbon refractories
镁炭质捣打料
5) Magnesitic Dry-Ramming Material
镁质干打料
1.
Application of Magnesitic Dry-Ramming Material for Bottom of A 50 t High Power EBT Arc Furnace;
镁质干打料在50tHP EBT电弧炉炉底上的应用
6) Magnesia based dry vibration mix
镁质干式料
1.
Magnesia based dry vibration mix was prepared using fused magnesia and sintered magnesia as the main staring materials,respectively,environmental friendly inorganic salt Na2SiO3·9H2O as binder.
9H2O的添加量(质量分数分别为4%、5%、6%、7%)对镁质干式料性能的影响,并采用静态坩埚法评价了试样的抗渣性能。
补充资料：捣打料
分子式：
CAS号：
性质：又称耐火捣打料,采用强力捣打方式制成的半干状态的散状耐火材料。一般要求具有高的体积稳定性、致密性和耐侵蚀性，用于感应电炉的捣打料还应具有绝缘性。它与浇注料或可塑料相比，其流动性很差，成型时必须强力捣打才能获得致密的结构。由具有一定粒度组成的耐火集料(骨料和粉料)、结合剂(无机胶结材料和焦油沥青)和外加剂组成。按所用的集料性质可分为：(1)酸性捣打料，主要用作工频感应炉内衬、玻璃熔窑窑底的内衬等；(2)中性捣打料，主要用作感应炉、加热炉和均热炉等烧嘴与内衬；(3)碱性捣打料，主要用作电炉和平炉炉底的内衬以及转炉炉衬的填料等；(4)含碳化硅、氮化硅和碳素捣打料，主要用作各类大、中、小高炉的出铁沟内衬。
CAS号：
性质：又称耐火捣打料,采用强力捣打方式制成的半干状态的散状耐火材料。一般要求具有高的体积稳定性、致密性和耐侵蚀性，用于感应电炉的捣打料还应具有绝缘性。它与浇注料或可塑料相比，其流动性很差，成型时必须强力捣打才能获得致密的结构。由具有一定粒度组成的耐火集料(骨料和粉料)、结合剂(无机胶结材料和焦油沥青)和外加剂组成。按所用的集料性质可分为：(1)酸性捣打料，主要用作工频感应炉内衬、玻璃熔窑窑底的内衬等；(2)中性捣打料，主要用作感应炉、加热炉和均热炉等烧嘴与内衬；(3)碱性捣打料，主要用作电炉和平炉炉底的内衬以及转炉炉衬的填料等；(4)含碳化硅、氮化硅和碳素捣打料，主要用作各类大、中、小高炉的出铁沟内衬。